In our previous paper [T. Matsushima et al., Nature 572, 502 (2019)], current densities of organic light-emitting diodes (OLEDs) did not decrease significantly when the thicknesses of a 1,4,5,8,9,11-hexaazatriphenylenehexacarbonitrile (HAT-CN) transport layer were increased from tens of nanometers to 1 μm. To make this mechanism clear, we carried out several experiments in terms of electron transfer with other organic layers and electron mobility of HAT-CN. Finally, we found that the vacuum-evaporated HAT-CN layers have very high electron mobility and, therefore, using a HAT-CN transport layer can suppress the decrease in current density even in thick OLEDs. The electron mobility of vacuum-deposited HAT-CN layers, which was measured using analysis with a space-charge-limited current model, was 0.1-1 cm2 V-1 s-1. This electron mobility is much higher than those of conventional organic transport layers used in OLEDs (<10-3 cm2 V-1 s-1) even though the HAT-CN layers are amorphous-like. We attributed one of the reasons for this extraordinarily high mobility to be a better overlap of πorbitals in the substrate normal, which is associated with horizontally oriented HAT-CN molecules on a substrate.
All Science Journal Classification (ASJC) codes
- Physics and Astronomy(all)