Anisotropic mechanical properties of ni-base superalloy compacts by direct laser forming technology

Naoto Yoshigai, Kentaro Kudo, Fujio Tsumori, Toshiko Osada, Hideshi Miura

Research output: Contribution to journalArticle

3 Citations (Scopus)

Abstract

As Ni-based superalloy has poor workability, direct laser forming (DLF) would be a powerful tool for fabricating the complex shaped Ni-based superalloy parts. We focused on the microstructure of the parts produced by DLF, the crystal grains of which grow along the building direction. This anisotropic microstructure is one of the major features of the parts produced by DLF, and which may cause anisotropic mechanical properties. In this work, the optimum laser-forming conditions such as laser power, laser scan speed, and powder feeding rate were determined by evaluating the density of the produced parts. Three types of tensile test pieces and two types of fatigue test pieces were fabricated in different building direction. They had higher ultimate tensile strength than that of JIS standards in wrought materials. However, their elongation was lower than that of JIS standards, and also the dispersion of elongation was large. On the other hand, fatigue limit was a little lower than the standard value. It was confirmed that the mechanical properties of Ni-based superalloy parts produced by DLF were different by a difference in building direction.

Original languageEnglish
Pages (from-to)427-433
Number of pages7
JournalFuntai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
Volume63
Issue number7
DOIs
Publication statusPublished - 2016

All Science Journal Classification (ASJC) codes

  • Mechanical Engineering
  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Anisotropic mechanical properties of ni-base superalloy compacts by direct laser forming technology'. Together they form a unique fingerprint.

  • Cite this