Brittle-to-ductile transition in martensite – bainite steel

Takumi Sakamaki, Masaki Tanaka, Tatsuya Morikawa, Hidenori Nako, Shigenobu Nanba

    Research output: Contribution to journalArticlepeer-review

    Abstract

    To understand the effect of composite structure on brittle-to-ductile transition (BDT) in low-carbon martensite–bainite steel, this study investigates the temperature dependence of the impact absorbed energy in five types of steel having the same chemical composition: fully martensitic steel, fully bainitic steel, and martensite–bainite steel with bainite fractions of 4%, 15%, and 55%, respectively. The BDT temperature was the highest for fully martensitic steel, followed by those of the martensite–4% bainite, martensite–15% bainite, martensite–55% bainite, and full bainitic steel. The BDT temperatures of martensite–15% bainite, martensite–55% bainite, and fully bainitic steel were close despite the large differences in their bainite volume fractions, suggesting that the trend of BDT temperatures cannot be explained simply based on the rule of mixture. The temperature dependence of 0.2% proof stress was measured in each steel to understand the trend of BDT temperature based on the shielding theory. Optical micrographs and the temperature dependence of effective stress indicated that the dislocations in bainite were preferentially activated and governed the yielding and BDT in the martensite-barite steels. This phenomenon was also linked to the network structures of bainite surrounding the martensite, where bainite was subjected to plastic deformation immediately after yielding in the employed steel.

    Original languageEnglish
    Pages (from-to)2167-2175
    Number of pages9
    Journalisij international
    Volume61
    Issue number7
    DOIs
    Publication statusPublished - 2021

    All Science Journal Classification (ASJC) codes

    • Mechanics of Materials
    • Mechanical Engineering
    • Metals and Alloys
    • Materials Chemistry

    Fingerprint

    Dive into the research topics of 'Brittle-to-ductile transition in martensite – bainite steel'. Together they form a unique fingerprint.

    Cite this