Catalyst deactivation in distillate hydrotreating (part 2) roman analysis of carbon deposited on hydrotreating catalyst for vacuum gas oil

Masaomi Amemiya, Yozo Korai, Isao Mochida

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

Carbon deposited on spent vacuum gas oil (VGO) hydrotreating catalysts from a commercial plant was investigated by elemental analysis and Raman spectroscopy. The samples of spent catalysts were separately recovered from the catalyst bed at several depths in the reactor after one year of commercial operation at 8 MPa, 360-400°C and LHSV 2 h-1. The amount of coke deposited increased with depth in the catalyst bed, whereas volatile components in the spent catalyst decreased. The Raman spectrum of the carbon deposits on all catalyst samples showed bands at 1600 cm-1 and 1350 cm-1, which became more pronounced at greater depths in the catalyst bed. Calcination of the catalyst at 500°C for 2 h under a nitrogen gas stream caused marked enhancement of the bands of coke on the catalysts recovered from the upper part of the bed, but had no effect on the bands of coke on the catalysts recovered from the lower part of the bed. The asphaltene fraction contaminated with VGO was adsorbed on the catalyst in the upper parts of catalyst bed and condensed at the designed reaction temperature. In contrast, the higher temperatures at the lower parts of the catalyst bed due to the heat released by the hydrogénation reaction had extensively carbonized the adsorbed VGO to form partially graphitized carbon on the catalyst surface. Raman spectroscopy indicated the reaction temperature at each location of the catalyst bed and the progress of exothermic reactions.

Original languageEnglish
Pages (from-to)99-104
Number of pages6
Journaljournal of the japan petroleum institute
Volume46
Issue number3
Publication statusPublished - Dec 1 2008

Fingerprint

Catalyst deactivation
Gas oils
Vacuum
Catalysts
Carbon
Coke
Raman spectroscopy
Exothermic reactions
Calcination
Temperature

All Science Journal Classification (ASJC) codes

  • Fuel Technology
  • Energy Engineering and Power Technology

Cite this

Catalyst deactivation in distillate hydrotreating (part 2) roman analysis of carbon deposited on hydrotreating catalyst for vacuum gas oil. / Amemiya, Masaomi; Korai, Yozo; Mochida, Isao.

In: journal of the japan petroleum institute, Vol. 46, No. 3, 01.12.2008, p. 99-104.

Research output: Contribution to journalArticle

@article{afe7d24f56d64323938813cf33e0ed67,
title = "Catalyst deactivation in distillate hydrotreating (part 2) roman analysis of carbon deposited on hydrotreating catalyst for vacuum gas oil",
abstract = "Carbon deposited on spent vacuum gas oil (VGO) hydrotreating catalysts from a commercial plant was investigated by elemental analysis and Raman spectroscopy. The samples of spent catalysts were separately recovered from the catalyst bed at several depths in the reactor after one year of commercial operation at 8 MPa, 360-400°C and LHSV 2 h-1. The amount of coke deposited increased with depth in the catalyst bed, whereas volatile components in the spent catalyst decreased. The Raman spectrum of the carbon deposits on all catalyst samples showed bands at 1600 cm-1 and 1350 cm-1, which became more pronounced at greater depths in the catalyst bed. Calcination of the catalyst at 500°C for 2 h under a nitrogen gas stream caused marked enhancement of the bands of coke on the catalysts recovered from the upper part of the bed, but had no effect on the bands of coke on the catalysts recovered from the lower part of the bed. The asphaltene fraction contaminated with VGO was adsorbed on the catalyst in the upper parts of catalyst bed and condensed at the designed reaction temperature. In contrast, the higher temperatures at the lower parts of the catalyst bed due to the heat released by the hydrog{\'e}nation reaction had extensively carbonized the adsorbed VGO to form partially graphitized carbon on the catalyst surface. Raman spectroscopy indicated the reaction temperature at each location of the catalyst bed and the progress of exothermic reactions.",
author = "Masaomi Amemiya and Yozo Korai and Isao Mochida",
year = "2008",
month = "12",
day = "1",
language = "English",
volume = "46",
pages = "99--104",
journal = "Journal of the Japan Petroleum Institute",
issn = "1346-8804",
publisher = "Japan Petroleum Institute",
number = "3",

}

TY - JOUR

T1 - Catalyst deactivation in distillate hydrotreating (part 2) roman analysis of carbon deposited on hydrotreating catalyst for vacuum gas oil

AU - Amemiya, Masaomi

AU - Korai, Yozo

AU - Mochida, Isao

PY - 2008/12/1

Y1 - 2008/12/1

N2 - Carbon deposited on spent vacuum gas oil (VGO) hydrotreating catalysts from a commercial plant was investigated by elemental analysis and Raman spectroscopy. The samples of spent catalysts were separately recovered from the catalyst bed at several depths in the reactor after one year of commercial operation at 8 MPa, 360-400°C and LHSV 2 h-1. The amount of coke deposited increased with depth in the catalyst bed, whereas volatile components in the spent catalyst decreased. The Raman spectrum of the carbon deposits on all catalyst samples showed bands at 1600 cm-1 and 1350 cm-1, which became more pronounced at greater depths in the catalyst bed. Calcination of the catalyst at 500°C for 2 h under a nitrogen gas stream caused marked enhancement of the bands of coke on the catalysts recovered from the upper part of the bed, but had no effect on the bands of coke on the catalysts recovered from the lower part of the bed. The asphaltene fraction contaminated with VGO was adsorbed on the catalyst in the upper parts of catalyst bed and condensed at the designed reaction temperature. In contrast, the higher temperatures at the lower parts of the catalyst bed due to the heat released by the hydrogénation reaction had extensively carbonized the adsorbed VGO to form partially graphitized carbon on the catalyst surface. Raman spectroscopy indicated the reaction temperature at each location of the catalyst bed and the progress of exothermic reactions.

AB - Carbon deposited on spent vacuum gas oil (VGO) hydrotreating catalysts from a commercial plant was investigated by elemental analysis and Raman spectroscopy. The samples of spent catalysts were separately recovered from the catalyst bed at several depths in the reactor after one year of commercial operation at 8 MPa, 360-400°C and LHSV 2 h-1. The amount of coke deposited increased with depth in the catalyst bed, whereas volatile components in the spent catalyst decreased. The Raman spectrum of the carbon deposits on all catalyst samples showed bands at 1600 cm-1 and 1350 cm-1, which became more pronounced at greater depths in the catalyst bed. Calcination of the catalyst at 500°C for 2 h under a nitrogen gas stream caused marked enhancement of the bands of coke on the catalysts recovered from the upper part of the bed, but had no effect on the bands of coke on the catalysts recovered from the lower part of the bed. The asphaltene fraction contaminated with VGO was adsorbed on the catalyst in the upper parts of catalyst bed and condensed at the designed reaction temperature. In contrast, the higher temperatures at the lower parts of the catalyst bed due to the heat released by the hydrogénation reaction had extensively carbonized the adsorbed VGO to form partially graphitized carbon on the catalyst surface. Raman spectroscopy indicated the reaction temperature at each location of the catalyst bed and the progress of exothermic reactions.

UR - http://www.scopus.com/inward/record.url?scp=66249131331&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=66249131331&partnerID=8YFLogxK

M3 - Article

VL - 46

SP - 99

EP - 104

JO - Journal of the Japan Petroleum Institute

JF - Journal of the Japan Petroleum Institute

SN - 1346-8804

IS - 3

ER -