Cathodic performance of VOPO4 with various crystal phases for Li ion rechargeable battery

Bustam M. Azmi, Tatsumi Ishihara, Hiroyasu Nishiguchi, Yusaku Takita

Research output: Contribution to journalArticle

49 Citations (Scopus)

Abstract

Cathodic performance of six different VOPO4 phases for Li ion rechargeable battery was investigated. It was found that VOPO4 exhibits a high flat discharge potential of 3.7 V for Li ion electrochemical intercalation and de-intercalation excepting for β- and -types. On the other hand, slightly higher flat discharge potential of 3.9 and 3.8 V was observed for β- and -types. Capacity for Li intercalation is strongly related with the crystal structure of VOPO4. In particular, δ-phase exhibits the largest reversible capacity of ca. 130 mAh/g among the examined VOPO4. High capacity for Li intercalation in δ-phase VOPO4 hardly decreased over 30 times of charge and discharge cycles. Although the reversible capacity decreased with increasing the current density for charge and discharge, large capacity of 80 mAh/g was still sustained at 0.4 mA/cm2 for δ-type VOPO4.

Original languageEnglish
Pages (from-to)165-170
Number of pages6
JournalElectrochimica Acta
Volume48
Issue number2
DOIs
Publication statusPublished - Nov 21 2002
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)
  • Analytical Chemistry
  • Electrochemistry

Fingerprint Dive into the research topics of 'Cathodic performance of VOPO4 with various crystal phases for Li ion rechargeable battery'. Together they form a unique fingerprint.

  • Cite this