Change in the microstructure and mechanical properties of drawn pearlitic steel with low-temperature aging

D. Hirakami, K. Ushioda, T. Manabe, K. Noguchi, K. Takai, Y. Hata, S. Hata, H. Nakashima

Research output: Contribution to journalConference articlepeer-review

1 Citation (Scopus)

Abstract

Hydrogen embrittlement is a serious problem in high-strength steels. Drawn pearlitic steel shows excellent resistance to hydrogen embrittlement despite its high strength, and aging treatment at a low temperature can simultaneously improve its strength and hydrogen-embrittlement resistance. To clarify the mechanism for this we have used thermal desorption analysis (TDA) and the newly developed precession electron diffraction analysis method in the transmission electron microscope. After aging at 100 °C for 10 min, the amount of hydrogen seen amount on the TDA curve reduced at around 100 °C. In contrast, when aging was performed at 300 °C, the hydrogen amount further reduced at around 100 °C and the unevenly deformed lamellar ferrite zone was locally recovered. For the samples that were aged at the low temperature, we confirmed that their yield strength and relaxation stress ratios increased simultaneously with improvement in the hydrogen-embrittlement property. We infer that segregation of carbon or formation of very fine carbide in dislocations during aging is the cause of these behaviors.

Original languageEnglish
Article number012026
JournalIOP Conference Series: Materials Science and Engineering
Volume219
Issue number1
DOIs
Publication statusPublished - Aug 1 2017
Event38th Riso International Symposium on Materials Science - Riso, Denmark
Duration: Sep 4 2017Sep 8 2017

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Engineering(all)

Fingerprint Dive into the research topics of 'Change in the microstructure and mechanical properties of drawn pearlitic steel with low-temperature aging'. Together they form a unique fingerprint.

Cite this