Changes in the crystallinity of hydroxyapatite powder and structure of enamel treated with several concentrations of ammonium hexafluorosilicate

Toshiyuki Suge, Kunio Ishikawa, Takashi Matsuo

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

Purpose: To evaluate the effects of changing concentrations of ammonium hexafluorosilicate [SiF: (NH4)2SiF6] solution on the crystallinity of hydroxyapatite powder (HAP) and structure of human enamel in order to overcome the tooth discoloration caused by diamine silver fluoride [AgF: (NH3)2AgF] application. Methods: HAP was treated with several concentrations of SiF solution (from 10 to 19,400 ppm) for 5 minutes. The crystallinity of the HAP before and after SiF treatment was then measured by powder X-ray diffraction (XRD) analysis. The angular width (β) of the 002 diffraction peak was measured at 1/2 the height of the maximum intensity. Also, enamel specimens were prepared from a human extracted tooth. Several concentrations of SiF solution were applied to polished or phosphoric acid etched enamel specimens. The enamel surface was then observed using scanning electron microscopy (SEM). Results: XRD peaks became sharper after SiF treatment indicating that the crystallinity of apatite powder was increased. The 1/ß value was increased from 2.8 ±0.1 to 4.3 ± 0.1 after treatment with 1,000 ppm SiF solution. The amount of CaF2 formed in HAP was gradually increased with increasing concentrations of SiF solution. The XRD pattern was consistent with CaF2 in case of over 9,000 ppm SiF solution. SEM photographs demonstrated that exposed enamel rods with acid etching were filled with CaF2-like precipitate after SiF treatment regardless of the concentration of SiF solution.

Original languageEnglish
Pages (from-to)299-302
Number of pages4
JournalAmerican journal of dentistry
Volume25
Issue number5
Publication statusPublished - Oct 1 2012

Fingerprint

Durapatite
Dental Enamel
Powders
X-Ray Diffraction
Electron Scanning Microscopy
Tooth Discoloration
Apatites
hexafluorosilicate
Tooth
Acids

All Science Journal Classification (ASJC) codes

  • Dentistry(all)

Cite this

Changes in the crystallinity of hydroxyapatite powder and structure of enamel treated with several concentrations of ammonium hexafluorosilicate. / Suge, Toshiyuki; Ishikawa, Kunio; Matsuo, Takashi.

In: American journal of dentistry, Vol. 25, No. 5, 01.10.2012, p. 299-302.

Research output: Contribution to journalArticle

@article{6c9b7878a0f841b1a54332227698071d,
title = "Changes in the crystallinity of hydroxyapatite powder and structure of enamel treated with several concentrations of ammonium hexafluorosilicate",
abstract = "Purpose: To evaluate the effects of changing concentrations of ammonium hexafluorosilicate [SiF: (NH4)2SiF6] solution on the crystallinity of hydroxyapatite powder (HAP) and structure of human enamel in order to overcome the tooth discoloration caused by diamine silver fluoride [AgF: (NH3)2AgF] application. Methods: HAP was treated with several concentrations of SiF solution (from 10 to 19,400 ppm) for 5 minutes. The crystallinity of the HAP before and after SiF treatment was then measured by powder X-ray diffraction (XRD) analysis. The angular width (β) of the 002 diffraction peak was measured at 1/2 the height of the maximum intensity. Also, enamel specimens were prepared from a human extracted tooth. Several concentrations of SiF solution were applied to polished or phosphoric acid etched enamel specimens. The enamel surface was then observed using scanning electron microscopy (SEM). Results: XRD peaks became sharper after SiF treatment indicating that the crystallinity of apatite powder was increased. The 1/{\ss} value was increased from 2.8 ±0.1 to 4.3 ± 0.1 after treatment with 1,000 ppm SiF solution. The amount of CaF2 formed in HAP was gradually increased with increasing concentrations of SiF solution. The XRD pattern was consistent with CaF2 in case of over 9,000 ppm SiF solution. SEM photographs demonstrated that exposed enamel rods with acid etching were filled with CaF2-like precipitate after SiF treatment regardless of the concentration of SiF solution.",
author = "Toshiyuki Suge and Kunio Ishikawa and Takashi Matsuo",
year = "2012",
month = "10",
day = "1",
language = "English",
volume = "25",
pages = "299--302",
journal = "American Journal of Dentistry",
issn = "0894-8275",
publisher = "Mosher and Linder, Inc",
number = "5",

}

TY - JOUR

T1 - Changes in the crystallinity of hydroxyapatite powder and structure of enamel treated with several concentrations of ammonium hexafluorosilicate

AU - Suge, Toshiyuki

AU - Ishikawa, Kunio

AU - Matsuo, Takashi

PY - 2012/10/1

Y1 - 2012/10/1

N2 - Purpose: To evaluate the effects of changing concentrations of ammonium hexafluorosilicate [SiF: (NH4)2SiF6] solution on the crystallinity of hydroxyapatite powder (HAP) and structure of human enamel in order to overcome the tooth discoloration caused by diamine silver fluoride [AgF: (NH3)2AgF] application. Methods: HAP was treated with several concentrations of SiF solution (from 10 to 19,400 ppm) for 5 minutes. The crystallinity of the HAP before and after SiF treatment was then measured by powder X-ray diffraction (XRD) analysis. The angular width (β) of the 002 diffraction peak was measured at 1/2 the height of the maximum intensity. Also, enamel specimens were prepared from a human extracted tooth. Several concentrations of SiF solution were applied to polished or phosphoric acid etched enamel specimens. The enamel surface was then observed using scanning electron microscopy (SEM). Results: XRD peaks became sharper after SiF treatment indicating that the crystallinity of apatite powder was increased. The 1/ß value was increased from 2.8 ±0.1 to 4.3 ± 0.1 after treatment with 1,000 ppm SiF solution. The amount of CaF2 formed in HAP was gradually increased with increasing concentrations of SiF solution. The XRD pattern was consistent with CaF2 in case of over 9,000 ppm SiF solution. SEM photographs demonstrated that exposed enamel rods with acid etching were filled with CaF2-like precipitate after SiF treatment regardless of the concentration of SiF solution.

AB - Purpose: To evaluate the effects of changing concentrations of ammonium hexafluorosilicate [SiF: (NH4)2SiF6] solution on the crystallinity of hydroxyapatite powder (HAP) and structure of human enamel in order to overcome the tooth discoloration caused by diamine silver fluoride [AgF: (NH3)2AgF] application. Methods: HAP was treated with several concentrations of SiF solution (from 10 to 19,400 ppm) for 5 minutes. The crystallinity of the HAP before and after SiF treatment was then measured by powder X-ray diffraction (XRD) analysis. The angular width (β) of the 002 diffraction peak was measured at 1/2 the height of the maximum intensity. Also, enamel specimens were prepared from a human extracted tooth. Several concentrations of SiF solution were applied to polished or phosphoric acid etched enamel specimens. The enamel surface was then observed using scanning electron microscopy (SEM). Results: XRD peaks became sharper after SiF treatment indicating that the crystallinity of apatite powder was increased. The 1/ß value was increased from 2.8 ±0.1 to 4.3 ± 0.1 after treatment with 1,000 ppm SiF solution. The amount of CaF2 formed in HAP was gradually increased with increasing concentrations of SiF solution. The XRD pattern was consistent with CaF2 in case of over 9,000 ppm SiF solution. SEM photographs demonstrated that exposed enamel rods with acid etching were filled with CaF2-like precipitate after SiF treatment regardless of the concentration of SiF solution.

UR - http://www.scopus.com/inward/record.url?scp=84869100325&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84869100325&partnerID=8YFLogxK

M3 - Article

C2 - 23243979

AN - SCOPUS:84869100325

VL - 25

SP - 299

EP - 302

JO - American Journal of Dentistry

JF - American Journal of Dentistry

SN - 0894-8275

IS - 5

ER -