"Cleanmix" HDX providing high green densities and "Cleanmix" LEX eliminating trouble in compaction process

Tomoshige Ono, Yukiko Ozaki

Research output: Contribution to journalArticle

Abstract

"Cleanmix" HDX providing high green densities, and "Cleanmix" LEX eliminating troubles at compaction process were developed for the purpose of corresponding to the high-strength and complicated form of sintered parts."Cleanmix" HDX realizes high green density, 7.3 Mg/m3, at 686 MPa, which is equal density obtained by warm compaction processes. For HDX, a compression process was analysed and the factor controlling green density was considered with the filling die density. And it was confirmed that the green density of HDX is not affected by die temperature. It was certified that the lubricant for LEX has high lubricity at low lubricant concentration.

Original languageEnglish
Pages (from-to)78-82
Number of pages5
JournalJFE Technical Report
Issue number16
Publication statusPublished - Mar 2011
Externally publishedYes

Fingerprint

Compaction
Lubricants
Temperature

All Science Journal Classification (ASJC) codes

  • Mechanical Engineering
  • Mechanics of Materials
  • Materials Chemistry
  • Metals and Alloys

Cite this

"Cleanmix" HDX providing high green densities and "Cleanmix" LEX eliminating trouble in compaction process. / Ono, Tomoshige; Ozaki, Yukiko.

In: JFE Technical Report, No. 16, 03.2011, p. 78-82.

Research output: Contribution to journalArticle

@article{fb7f3c6f72fc4689aa8c9eb486272898,
title = "{"}Cleanmix{"} HDX providing high green densities and {"}Cleanmix{"} LEX eliminating trouble in compaction process",
abstract = "{"}Cleanmix{"} HDX providing high green densities, and {"}Cleanmix{"} LEX eliminating troubles at compaction process were developed for the purpose of corresponding to the high-strength and complicated form of sintered parts.{"}Cleanmix{"} HDX realizes high green density, 7.3 Mg/m3, at 686 MPa, which is equal density obtained by warm compaction processes. For HDX, a compression process was analysed and the factor controlling green density was considered with the filling die density. And it was confirmed that the green density of HDX is not affected by die temperature. It was certified that the lubricant for LEX has high lubricity at low lubricant concentration.",
author = "Tomoshige Ono and Yukiko Ozaki",
year = "2011",
month = "3",
language = "English",
pages = "78--82",
journal = "JFE Technical Report",
issn = "1348-0677",
publisher = "The Institute of Image Information and Television Engineers",
number = "16",

}

TY - JOUR

T1 - "Cleanmix" HDX providing high green densities and "Cleanmix" LEX eliminating trouble in compaction process

AU - Ono, Tomoshige

AU - Ozaki, Yukiko

PY - 2011/3

Y1 - 2011/3

N2 - "Cleanmix" HDX providing high green densities, and "Cleanmix" LEX eliminating troubles at compaction process were developed for the purpose of corresponding to the high-strength and complicated form of sintered parts."Cleanmix" HDX realizes high green density, 7.3 Mg/m3, at 686 MPa, which is equal density obtained by warm compaction processes. For HDX, a compression process was analysed and the factor controlling green density was considered with the filling die density. And it was confirmed that the green density of HDX is not affected by die temperature. It was certified that the lubricant for LEX has high lubricity at low lubricant concentration.

AB - "Cleanmix" HDX providing high green densities, and "Cleanmix" LEX eliminating troubles at compaction process were developed for the purpose of corresponding to the high-strength and complicated form of sintered parts."Cleanmix" HDX realizes high green density, 7.3 Mg/m3, at 686 MPa, which is equal density obtained by warm compaction processes. For HDX, a compression process was analysed and the factor controlling green density was considered with the filling die density. And it was confirmed that the green density of HDX is not affected by die temperature. It was certified that the lubricant for LEX has high lubricity at low lubricant concentration.

UR - http://www.scopus.com/inward/record.url?scp=79958054905&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=79958054905&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:79958054905

SP - 78

EP - 82

JO - JFE Technical Report

JF - JFE Technical Report

SN - 1348-0677

IS - 16

ER -