Correlation of hardening and microstructure of tantalum irradiated with heavy ions

Takeo Muroga, Kazufumi Yasunaga, Yutai Katoh, Hideo Watanabe, Naoaki Yoshida, Nobuaki Noda

Research output: Contribution to journalConference article

3 Citations (Scopus)

Abstract

The microhardness change of tantalum irradiated with heavy ions has been evaluated using a micro-indentation technique. The increase in hardness by irradiation was significant below approximately 900 K and negligible above approximately 1100 K. The hardness decreased steeply with temperature at approximately 1000 K. Correlation of the results with microstructure data showed that the strength of voids and line dislocations as barriers against deformation should be very weak relative to that of loops and TEM-invisible defects. The temperature and fluence dependence of the hardening by TEM-invisible defects, derived by the correlation, implied an accumulation process of cascade vacancy clusters during irradiation.

Original languageEnglish
Pages (from-to)1186-1196
Number of pages11
JournalASTM Special Technical Publication
Issue number1366
Publication statusPublished - Dec 1 2000
Event19th International Symposium: Effects of Radiation on Materials - Seattle, WA, USA
Duration: Jun 16 1998Jun 18 1998

All Science Journal Classification (ASJC) codes

  • Engineering(all)

Fingerprint Dive into the research topics of 'Correlation of hardening and microstructure of tantalum irradiated with heavy ions'. Together they form a unique fingerprint.

  • Cite this

    Muroga, T., Yasunaga, K., Katoh, Y., Watanabe, H., Yoshida, N., & Noda, N. (2000). Correlation of hardening and microstructure of tantalum irradiated with heavy ions. ASTM Special Technical Publication, (1366), 1186-1196.