Critical current enhancement in PLD YBa2Cu3O7-x films using artificial pinning centers

P. Mele, K. Matsumoto, T. Horide, O. Miura, A. Ichinose, M. Mukaida, Y. Yoshida, S. Horii

    Research output: Contribution to journalArticlepeer-review

    15 Citations (Scopus)

    Abstract

    We introduced high-density columnar defects as artificial pinning centers (APCs) for quantized vortices into YBa2Cu3O7-x (YBCO) films during the film deposition procedure. APCs were introduced perpendicular to the film surface using nano-sized Y2O3 islands prepared on SrTiO3(1 0 0) substrates. Varying the deposition parameters and the substrate annealing conditions allowed strong changes in the shape and density of the Y2O3 islands to be induced. Compared to a pure YBCO film, the best performance among the APCs samples was obtained on the Y2O3-deposited substrate with 5 laser pulses, corresponding to a nominal thickness of 0.2 nm. Even when the APC films were prepared using the same deposition conditions, the columnar defects enhanced Jc at 77 K from 1.8 to 2.7 MA/cm2 (self field) and from 0.06 to 0.10 MA/cm2 (H = 5 T, H∥c-axis).

    Original languageEnglish
    Pages (from-to)648-651
    Number of pages4
    JournalPhysica C: Superconductivity and its applications
    Volume445-448
    Issue number1-2
    DOIs
    Publication statusPublished - Oct 1 2006

    All Science Journal Classification (ASJC) codes

    • Electronic, Optical and Magnetic Materials
    • Condensed Matter Physics
    • Energy Engineering and Power Technology
    • Electrical and Electronic Engineering

    Fingerprint

    Dive into the research topics of 'Critical current enhancement in PLD YBa2Cu3O7-x films using artificial pinning centers'. Together they form a unique fingerprint.

    Cite this