Deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating

Shigenobu Kainuma, Jinxuan Du, Muye Yang, Kazuyoshi Muto, Hirokazu Miyata

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

The objective of this study is to clarify the deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating. Combined cyclic corrosion tests were carried out on common carbon steel plates with overlapping layers. To evaluate the effective area of the sacrificial anode reaction caused by the thermal spray coating, machined straight-line defects with widths of 0.2, 6 and 12 mm were introduced in the overlapping layer. The experimental results indicated that the layers began to deteriorate from the lower part of the thermal spray coating along the defects. The deterioration of the thermal spray coating was accelerated by the sealing treatment. The blister area and height at the overlapping layer were significantly different depending on the sealing treatment.

Original languageEnglish
Title of host publicationAdvances in Fracture and Damage Mechanics XVI - 16th FDM
EditorsSergio Baragetti, Ferri M.H. Aliabadi, Paolo Maria Mariano, Katia Casavola, Carmine Pappalettere
PublisherTrans Tech Publications Ltd
Pages55-58
Number of pages4
ISBN (Print)9783035711684
DOIs
Publication statusPublished - Jan 1 2017
Event16th International Conference on Fracture and Damage Mechanics, 2017 - Florence, Italy
Duration: Jul 18 2017Jul 20 2017

Publication series

NameKey Engineering Materials
Volume754 KEM
ISSN (Print)1013-9826

Other

Other16th International Conference on Fracture and Damage Mechanics, 2017
CountryItaly
CityFlorence
Period7/18/177/20/17

Fingerprint

Paint
Deterioration
Coatings
Defects
Carbon steel
Anodes
Hot Temperature
Corrosion

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Kainuma, S., Du, J., Yang, M., Muto, K., & Miyata, H. (2017). Deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating. In S. Baragetti, F. M. H. Aliabadi, P. M. Mariano, K. Casavola, & C. Pappalettere (Eds.), Advances in Fracture and Damage Mechanics XVI - 16th FDM (pp. 55-58). (Key Engineering Materials; Vol. 754 KEM). Trans Tech Publications Ltd. https://doi.org/10.4028/www.scientific.net/KEM.754.55

Deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating. / Kainuma, Shigenobu; Du, Jinxuan; Yang, Muye; Muto, Kazuyoshi; Miyata, Hirokazu.

Advances in Fracture and Damage Mechanics XVI - 16th FDM. ed. / Sergio Baragetti; Ferri M.H. Aliabadi; Paolo Maria Mariano; Katia Casavola; Carmine Pappalettere. Trans Tech Publications Ltd, 2017. p. 55-58 (Key Engineering Materials; Vol. 754 KEM).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Kainuma, S, Du, J, Yang, M, Muto, K & Miyata, H 2017, Deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating. in S Baragetti, FMH Aliabadi, PM Mariano, K Casavola & C Pappalettere (eds), Advances in Fracture and Damage Mechanics XVI - 16th FDM. Key Engineering Materials, vol. 754 KEM, Trans Tech Publications Ltd, pp. 55-58, 16th International Conference on Fracture and Damage Mechanics, 2017, Florence, Italy, 7/18/17. https://doi.org/10.4028/www.scientific.net/KEM.754.55
Kainuma S, Du J, Yang M, Muto K, Miyata H. Deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating. In Baragetti S, Aliabadi FMH, Mariano PM, Casavola K, Pappalettere C, editors, Advances in Fracture and Damage Mechanics XVI - 16th FDM. Trans Tech Publications Ltd. 2017. p. 55-58. (Key Engineering Materials). https://doi.org/10.4028/www.scientific.net/KEM.754.55
Kainuma, Shigenobu ; Du, Jinxuan ; Yang, Muye ; Muto, Kazuyoshi ; Miyata, Hirokazu. / Deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating. Advances in Fracture and Damage Mechanics XVI - 16th FDM. editor / Sergio Baragetti ; Ferri M.H. Aliabadi ; Paolo Maria Mariano ; Katia Casavola ; Carmine Pappalettere. Trans Tech Publications Ltd, 2017. pp. 55-58 (Key Engineering Materials).
@inproceedings{2997e715de6043b8beae0d66cde161e3,
title = "Deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating",
abstract = "The objective of this study is to clarify the deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating. Combined cyclic corrosion tests were carried out on common carbon steel plates with overlapping layers. To evaluate the effective area of the sacrificial anode reaction caused by the thermal spray coating, machined straight-line defects with widths of 0.2, 6 and 12 mm were introduced in the overlapping layer. The experimental results indicated that the layers began to deteriorate from the lower part of the thermal spray coating along the defects. The deterioration of the thermal spray coating was accelerated by the sealing treatment. The blister area and height at the overlapping layer were significantly different depending on the sealing treatment.",
author = "Shigenobu Kainuma and Jinxuan Du and Muye Yang and Kazuyoshi Muto and Hirokazu Miyata",
year = "2017",
month = "1",
day = "1",
doi = "10.4028/www.scientific.net/KEM.754.55",
language = "English",
isbn = "9783035711684",
series = "Key Engineering Materials",
publisher = "Trans Tech Publications Ltd",
pages = "55--58",
editor = "Sergio Baragetti and Aliabadi, {Ferri M.H.} and Mariano, {Paolo Maria} and Katia Casavola and Carmine Pappalettere",
booktitle = "Advances in Fracture and Damage Mechanics XVI - 16th FDM",

}

TY - GEN

T1 - Deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating

AU - Kainuma, Shigenobu

AU - Du, Jinxuan

AU - Yang, Muye

AU - Muto, Kazuyoshi

AU - Miyata, Hirokazu

PY - 2017/1/1

Y1 - 2017/1/1

N2 - The objective of this study is to clarify the deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating. Combined cyclic corrosion tests were carried out on common carbon steel plates with overlapping layers. To evaluate the effective area of the sacrificial anode reaction caused by the thermal spray coating, machined straight-line defects with widths of 0.2, 6 and 12 mm were introduced in the overlapping layer. The experimental results indicated that the layers began to deteriorate from the lower part of the thermal spray coating along the defects. The deterioration of the thermal spray coating was accelerated by the sealing treatment. The blister area and height at the overlapping layer were significantly different depending on the sealing treatment.

AB - The objective of this study is to clarify the deterioration behaviors of overlapping layers between Al-5Mg alloy thermal spray coating and heavy-duty paint coating. Combined cyclic corrosion tests were carried out on common carbon steel plates with overlapping layers. To evaluate the effective area of the sacrificial anode reaction caused by the thermal spray coating, machined straight-line defects with widths of 0.2, 6 and 12 mm were introduced in the overlapping layer. The experimental results indicated that the layers began to deteriorate from the lower part of the thermal spray coating along the defects. The deterioration of the thermal spray coating was accelerated by the sealing treatment. The blister area and height at the overlapping layer were significantly different depending on the sealing treatment.

UR - http://www.scopus.com/inward/record.url?scp=85029894530&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85029894530&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/KEM.754.55

DO - 10.4028/www.scientific.net/KEM.754.55

M3 - Conference contribution

AN - SCOPUS:85029894530

SN - 9783035711684

T3 - Key Engineering Materials

SP - 55

EP - 58

BT - Advances in Fracture and Damage Mechanics XVI - 16th FDM

A2 - Baragetti, Sergio

A2 - Aliabadi, Ferri M.H.

A2 - Mariano, Paolo Maria

A2 - Casavola, Katia

A2 - Pappalettere, Carmine

PB - Trans Tech Publications Ltd

ER -