Dissolution rate of silicon nitride ceramics into molten CaO-Al2O3-SiO2 slags

Shoichirou Taira, Yasuyuki Yamasaki, Kunihiko Nakashima, Katsumi Mori

    Research output: Contribution to journalArticlepeer-review

    7 Citations (Scopus)

    Abstract

    The dissolution rates of silicon nitride (Si3N4) ceramics into CaO-Al2O3-SiO2 slags were investigated by using a rotating specimen method in the temperature range of 1773-1873 K. Dissolution rates in the present study increased as the revolution speed and temperature increased and decreased as the SiO2 content of the slags increased. The nitrogen content of the slags increased after the Si3N4 ceramics had been immersed into them. The slags contained two types of nitrogen ions - N3- and CN- - because a graphite crucible was used for the experiment. N3- ions were confirmed in all the slags that were used in the present work; the CN- content was much lower than that of the N3- ions, except in the slag without SiO2. Based on those results, Fick's law of diffusion was used to analyze the dissolution rates. The dissolution mechanism of the Si3N4 ceramics into CaO-Al2O3-SiO2 slags has been discussed in this paper.

    Original languageEnglish
    Pages (from-to)925-932
    Number of pages8
    JournalJournal of the American Ceramic Society
    Volume80
    Issue number4
    DOIs
    Publication statusPublished - Apr 1997

    All Science Journal Classification (ASJC) codes

    • Ceramics and Composites
    • Materials Chemistry

    Fingerprint Dive into the research topics of 'Dissolution rate of silicon nitride ceramics into molten CaO-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> slags'. Together they form a unique fingerprint.

    Cite this