Dynamic light scattering and dynamic viscoelasticity of poly(vinyl alcohol) in aqueous borax solutions. 5. Temperature effects

Kazuki Koga, Akihiko Takada, Norio Nemoto

Research output: Contribution to journalArticle

26 Citations (Scopus)

Abstract

Steady viscosity, dynamic viscoelasticity (DVE), and dynamic light scattering (DLS) measurements were made to study the effects of temperature, T, on association behaviors of poly(vinyl alcohol) (PVA) with weight-average degree of polymerization DPw = 350 in aqueous Borax solution. Intrinsic viscosity, [r/], monotonically decreased by 23% with a rise in T from 10 to 65 °C. At low T, enhancement in viscosity was observed with increasing polymer concentration, C, due to formation of viscoelastic network with the didiol complex as temporal cross-links, and the time-temperature superposition principle was found to be applicable for construction of a composite curve at each C. Those composite curves were further reduced so as to give one master curve. The system tended to lose its viscoelastic nature, when raising the temperature, toward a viscous solution owing to a decrease in the number of the didiol complexes as well as the shrinkage of the PVA chains. We found from analysis of DVE and DLS data that a clear boundary line between viscoelastic and viscous behaviors can be drawn on the T-C diagram using the temperature TN defined as the inflection point in a η vs T-1 plot for each C.

Original languageEnglish
Pages (from-to)8872-8879
Number of pages8
JournalMacromolecules
Volume32
Issue number26
DOIs
Publication statusPublished - Dec 28 1999

All Science Journal Classification (ASJC) codes

  • Organic Chemistry
  • Polymers and Plastics
  • Inorganic Chemistry
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Dynamic light scattering and dynamic viscoelasticity of poly(vinyl alcohol) in aqueous borax solutions. 5. Temperature effects'. Together they form a unique fingerprint.

  • Cite this