Effect of aluminum sulfate on dispersion state of sodium carboxymethylcellulose in aqueous solution

Daisuke Ishii, Daisuke Tatsumi, Takayoshi Matsumoto

Research output: Contribution to journalArticle

4 Citations (Scopus)

Abstract

Effect of aluminum sulfate, Al2(SO4)3, on dispersion state of sodium carboxymethylcellulose, NaCMC, in aqueous solution was investigated by rheological measurements and X-ray photoelectron spectroscopy (XPS). Rheological properties of NaCMC aqueous solutions containing Al2(SO4)3 were investigated using a cone-plate type rheometer. When NaCMC concentration was 0.5 wt %, shear stress of the solution slightly decreased with increasing concentration of Al2(SO4)3. On the other hand, when NaCMC concentration was 5 wt %, the shear stress increased with increasing Al2(SO4)3 concentration. In this case, both dynamic storage and loss moduli also increased. These results suggest that the addition of Al2(SO4)3 increased crosslinking density and caused heterogeneous aggregation of NaCMC. This was confirmed by the fact that diluted Al2(SO4)3-containing NaCMC solution was separated to microgel-like particle and homogeneous solution. XPS revealed that aluminum ion was concentrated in the microgel-like particle. From these results, dispersion state of NaCMC in aqueous solution containing Al2(SO4)3 was modeled as microgel-like particle containing concentrated aluminum ions are suspended in the network of NaCMC chains.

Original languageEnglish
Pages (from-to)267-272
Number of pages6
JournalNihon Reoroji Gakkaishi
Volume40
Issue number5
DOIs
Publication statusPublished - Dec 1 2012

Fingerprint

Carboxymethylcellulose Sodium
sulfates
Sodium
sodium
aqueous solutions
aluminum
Aluminum
shear stress
photoelectron spectroscopy
rheometers
Shear stress
crosslinking
X ray photoelectron spectroscopy
Ions
cones
ions
x rays
Rheometers
Crosslinking
aluminum sulfate

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Effect of aluminum sulfate on dispersion state of sodium carboxymethylcellulose in aqueous solution. / Ishii, Daisuke; Tatsumi, Daisuke; Matsumoto, Takayoshi.

In: Nihon Reoroji Gakkaishi, Vol. 40, No. 5, 01.12.2012, p. 267-272.

Research output: Contribution to journalArticle

@article{c6163ba9f83742d588219aa71f93a582,
title = "Effect of aluminum sulfate on dispersion state of sodium carboxymethylcellulose in aqueous solution",
abstract = "Effect of aluminum sulfate, Al2(SO4)3, on dispersion state of sodium carboxymethylcellulose, NaCMC, in aqueous solution was investigated by rheological measurements and X-ray photoelectron spectroscopy (XPS). Rheological properties of NaCMC aqueous solutions containing Al2(SO4)3 were investigated using a cone-plate type rheometer. When NaCMC concentration was 0.5 wt {\%}, shear stress of the solution slightly decreased with increasing concentration of Al2(SO4)3. On the other hand, when NaCMC concentration was 5 wt {\%}, the shear stress increased with increasing Al2(SO4)3 concentration. In this case, both dynamic storage and loss moduli also increased. These results suggest that the addition of Al2(SO4)3 increased crosslinking density and caused heterogeneous aggregation of NaCMC. This was confirmed by the fact that diluted Al2(SO4)3-containing NaCMC solution was separated to microgel-like particle and homogeneous solution. XPS revealed that aluminum ion was concentrated in the microgel-like particle. From these results, dispersion state of NaCMC in aqueous solution containing Al2(SO4)3 was modeled as microgel-like particle containing concentrated aluminum ions are suspended in the network of NaCMC chains.",
author = "Daisuke Ishii and Daisuke Tatsumi and Takayoshi Matsumoto",
year = "2012",
month = "12",
day = "1",
doi = "10.1678/rheology.40.267",
language = "English",
volume = "40",
pages = "267--272",
journal = "Nihon Reoroji Gakkaishi",
issn = "0387-1533",
publisher = "Society of Rheology",
number = "5",

}

TY - JOUR

T1 - Effect of aluminum sulfate on dispersion state of sodium carboxymethylcellulose in aqueous solution

AU - Ishii, Daisuke

AU - Tatsumi, Daisuke

AU - Matsumoto, Takayoshi

PY - 2012/12/1

Y1 - 2012/12/1

N2 - Effect of aluminum sulfate, Al2(SO4)3, on dispersion state of sodium carboxymethylcellulose, NaCMC, in aqueous solution was investigated by rheological measurements and X-ray photoelectron spectroscopy (XPS). Rheological properties of NaCMC aqueous solutions containing Al2(SO4)3 were investigated using a cone-plate type rheometer. When NaCMC concentration was 0.5 wt %, shear stress of the solution slightly decreased with increasing concentration of Al2(SO4)3. On the other hand, when NaCMC concentration was 5 wt %, the shear stress increased with increasing Al2(SO4)3 concentration. In this case, both dynamic storage and loss moduli also increased. These results suggest that the addition of Al2(SO4)3 increased crosslinking density and caused heterogeneous aggregation of NaCMC. This was confirmed by the fact that diluted Al2(SO4)3-containing NaCMC solution was separated to microgel-like particle and homogeneous solution. XPS revealed that aluminum ion was concentrated in the microgel-like particle. From these results, dispersion state of NaCMC in aqueous solution containing Al2(SO4)3 was modeled as microgel-like particle containing concentrated aluminum ions are suspended in the network of NaCMC chains.

AB - Effect of aluminum sulfate, Al2(SO4)3, on dispersion state of sodium carboxymethylcellulose, NaCMC, in aqueous solution was investigated by rheological measurements and X-ray photoelectron spectroscopy (XPS). Rheological properties of NaCMC aqueous solutions containing Al2(SO4)3 were investigated using a cone-plate type rheometer. When NaCMC concentration was 0.5 wt %, shear stress of the solution slightly decreased with increasing concentration of Al2(SO4)3. On the other hand, when NaCMC concentration was 5 wt %, the shear stress increased with increasing Al2(SO4)3 concentration. In this case, both dynamic storage and loss moduli also increased. These results suggest that the addition of Al2(SO4)3 increased crosslinking density and caused heterogeneous aggregation of NaCMC. This was confirmed by the fact that diluted Al2(SO4)3-containing NaCMC solution was separated to microgel-like particle and homogeneous solution. XPS revealed that aluminum ion was concentrated in the microgel-like particle. From these results, dispersion state of NaCMC in aqueous solution containing Al2(SO4)3 was modeled as microgel-like particle containing concentrated aluminum ions are suspended in the network of NaCMC chains.

UR - http://www.scopus.com/inward/record.url?scp=84873926001&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84873926001&partnerID=8YFLogxK

U2 - 10.1678/rheology.40.267

DO - 10.1678/rheology.40.267

M3 - Article

AN - SCOPUS:84873926001

VL - 40

SP - 267

EP - 272

JO - Nihon Reoroji Gakkaishi

JF - Nihon Reoroji Gakkaishi

SN - 0387-1533

IS - 5

ER -