Effect of metal composition ratios of solutions on Jc-B properties of REBCO coated conductors fabricated by advanced TFA-MOD process

Y. Kitoh, Junko Matsuda, K. Suzuki, K. Nakaoka, Y. Sutoh, A. Nakai, T. Nakanishi, M. Yoshizumi, T. Machi, A. Yajima, Y. Yamada, T. Izumi, Y. Shiohara

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

Metal organic deposition using trifluoroacetates (TFA-MOD) is expected as a low cost process of high Tc superconducting coated conductors, since this method does not need any high vacuum system. The advanced TFA-MOD process enabled us to produce YBa2Cu3O7-y (YBCO) films on IBAD buffered metallic substrates (PLD-CeO2/IBAD-GZO/Hastelloy) with high critical current density (Jc) values over 2 MA/cm2 under the conditions of T = 77 K and the self fields. REBCO (RE:Y and Sm) films with different compositions were fabricated on the substrates by the advanced TFA-MOD process using TFA salts of Y, Sm, Ba and Cu-Naphthenate. The films which had excess amounts of (Sm), (Sm and Cu) or (Y and Cu) in addition to the stoichiometric 123 composition (Y:Ba:Cu = 1:2:3) showed higher Jc values (>3 MA/cm2) at 77 K under the self fields compared with that of the stoichiometric composition film. In addition, the Jc values of the (Sm) or (Sm and Cu) added films were also improved under the high magnetic fields compared with that of the stoichiometric composition film. The origins of pinning centers were discussed from the perspectives of microstructures, crystal growth mechanisms, and so on.

Original languageEnglish
Pages (from-to)523-526
Number of pages4
JournalPhysica C: Superconductivity and its Applications
Volume463-465
Issue numberSUPPL.
DOIs
Publication statusPublished - Oct 1 2007
Externally publishedYes

Fingerprint

conductors
Metals
Chemical analysis
metals
Ion beam assisted deposition
Hastelloy (trademark)
Trifluoroacetic Acid
vacuum systems
Substrates
Pulsed laser deposition
high vacuum
Crystallization
Crystal growth
crystal growth
critical current
Salts
Vacuum
Magnetic fields
current density
salts

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering

Cite this

Effect of metal composition ratios of solutions on Jc-B properties of REBCO coated conductors fabricated by advanced TFA-MOD process. / Kitoh, Y.; Matsuda, Junko; Suzuki, K.; Nakaoka, K.; Sutoh, Y.; Nakai, A.; Nakanishi, T.; Yoshizumi, M.; Machi, T.; Yajima, A.; Yamada, Y.; Izumi, T.; Shiohara, Y.

In: Physica C: Superconductivity and its Applications, Vol. 463-465, No. SUPPL., 01.10.2007, p. 523-526.

Research output: Contribution to journalArticle

Kitoh, Y, Matsuda, J, Suzuki, K, Nakaoka, K, Sutoh, Y, Nakai, A, Nakanishi, T, Yoshizumi, M, Machi, T, Yajima, A, Yamada, Y, Izumi, T & Shiohara, Y 2007, 'Effect of metal composition ratios of solutions on Jc-B properties of REBCO coated conductors fabricated by advanced TFA-MOD process', Physica C: Superconductivity and its Applications, vol. 463-465, no. SUPPL., pp. 523-526. https://doi.org/10.1016/j.physc.2007.04.241
Kitoh, Y. ; Matsuda, Junko ; Suzuki, K. ; Nakaoka, K. ; Sutoh, Y. ; Nakai, A. ; Nakanishi, T. ; Yoshizumi, M. ; Machi, T. ; Yajima, A. ; Yamada, Y. ; Izumi, T. ; Shiohara, Y. / Effect of metal composition ratios of solutions on Jc-B properties of REBCO coated conductors fabricated by advanced TFA-MOD process. In: Physica C: Superconductivity and its Applications. 2007 ; Vol. 463-465, No. SUPPL. pp. 523-526.
@article{e62dbf8141264f1c86ad86eb8b496481,
title = "Effect of metal composition ratios of solutions on Jc-B properties of REBCO coated conductors fabricated by advanced TFA-MOD process",
abstract = "Metal organic deposition using trifluoroacetates (TFA-MOD) is expected as a low cost process of high Tc superconducting coated conductors, since this method does not need any high vacuum system. The advanced TFA-MOD process enabled us to produce YBa2Cu3O7-y (YBCO) films on IBAD buffered metallic substrates (PLD-CeO2/IBAD-GZO/Hastelloy) with high critical current density (Jc) values over 2 MA/cm2 under the conditions of T = 77 K and the self fields. REBCO (RE:Y and Sm) films with different compositions were fabricated on the substrates by the advanced TFA-MOD process using TFA salts of Y, Sm, Ba and Cu-Naphthenate. The films which had excess amounts of (Sm), (Sm and Cu) or (Y and Cu) in addition to the stoichiometric 123 composition (Y:Ba:Cu = 1:2:3) showed higher Jc values (>3 MA/cm2) at 77 K under the self fields compared with that of the stoichiometric composition film. In addition, the Jc values of the (Sm) or (Sm and Cu) added films were also improved under the high magnetic fields compared with that of the stoichiometric composition film. The origins of pinning centers were discussed from the perspectives of microstructures, crystal growth mechanisms, and so on.",
author = "Y. Kitoh and Junko Matsuda and K. Suzuki and K. Nakaoka and Y. Sutoh and A. Nakai and T. Nakanishi and M. Yoshizumi and T. Machi and A. Yajima and Y. Yamada and T. Izumi and Y. Shiohara",
year = "2007",
month = "10",
day = "1",
doi = "10.1016/j.physc.2007.04.241",
language = "English",
volume = "463-465",
pages = "523--526",
journal = "Physica C: Superconductivity and its Applications",
issn = "0921-4534",
publisher = "Elsevier",
number = "SUPPL.",

}

TY - JOUR

T1 - Effect of metal composition ratios of solutions on Jc-B properties of REBCO coated conductors fabricated by advanced TFA-MOD process

AU - Kitoh, Y.

AU - Matsuda, Junko

AU - Suzuki, K.

AU - Nakaoka, K.

AU - Sutoh, Y.

AU - Nakai, A.

AU - Nakanishi, T.

AU - Yoshizumi, M.

AU - Machi, T.

AU - Yajima, A.

AU - Yamada, Y.

AU - Izumi, T.

AU - Shiohara, Y.

PY - 2007/10/1

Y1 - 2007/10/1

N2 - Metal organic deposition using trifluoroacetates (TFA-MOD) is expected as a low cost process of high Tc superconducting coated conductors, since this method does not need any high vacuum system. The advanced TFA-MOD process enabled us to produce YBa2Cu3O7-y (YBCO) films on IBAD buffered metallic substrates (PLD-CeO2/IBAD-GZO/Hastelloy) with high critical current density (Jc) values over 2 MA/cm2 under the conditions of T = 77 K and the self fields. REBCO (RE:Y and Sm) films with different compositions were fabricated on the substrates by the advanced TFA-MOD process using TFA salts of Y, Sm, Ba and Cu-Naphthenate. The films which had excess amounts of (Sm), (Sm and Cu) or (Y and Cu) in addition to the stoichiometric 123 composition (Y:Ba:Cu = 1:2:3) showed higher Jc values (>3 MA/cm2) at 77 K under the self fields compared with that of the stoichiometric composition film. In addition, the Jc values of the (Sm) or (Sm and Cu) added films were also improved under the high magnetic fields compared with that of the stoichiometric composition film. The origins of pinning centers were discussed from the perspectives of microstructures, crystal growth mechanisms, and so on.

AB - Metal organic deposition using trifluoroacetates (TFA-MOD) is expected as a low cost process of high Tc superconducting coated conductors, since this method does not need any high vacuum system. The advanced TFA-MOD process enabled us to produce YBa2Cu3O7-y (YBCO) films on IBAD buffered metallic substrates (PLD-CeO2/IBAD-GZO/Hastelloy) with high critical current density (Jc) values over 2 MA/cm2 under the conditions of T = 77 K and the self fields. REBCO (RE:Y and Sm) films with different compositions were fabricated on the substrates by the advanced TFA-MOD process using TFA salts of Y, Sm, Ba and Cu-Naphthenate. The films which had excess amounts of (Sm), (Sm and Cu) or (Y and Cu) in addition to the stoichiometric 123 composition (Y:Ba:Cu = 1:2:3) showed higher Jc values (>3 MA/cm2) at 77 K under the self fields compared with that of the stoichiometric composition film. In addition, the Jc values of the (Sm) or (Sm and Cu) added films were also improved under the high magnetic fields compared with that of the stoichiometric composition film. The origins of pinning centers were discussed from the perspectives of microstructures, crystal growth mechanisms, and so on.

UR - http://www.scopus.com/inward/record.url?scp=34548441694&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=34548441694&partnerID=8YFLogxK

U2 - 10.1016/j.physc.2007.04.241

DO - 10.1016/j.physc.2007.04.241

M3 - Article

VL - 463-465

SP - 523

EP - 526

JO - Physica C: Superconductivity and its Applications

JF - Physica C: Superconductivity and its Applications

SN - 0921-4534

IS - SUPPL.

ER -