Effect of nitrogen on tensile deformation behavior and development of deformation structure in titanium

Tomohiro Ando, Toshihiro Tsuchiyama, Setsuo Takaki

Research output: Contribution to journalArticle

6 Citations (Scopus)

Abstract

Ti-N alloys with different nitrogen content were tensile-tested, and then the effect of nitrogen on tensile properties and deformation structure were investigated. With increasing nitrogen content, the 0.2% proof stress and tensile stress were markedly increased accompanied with the lattice distortion of enlargement of c/a ratio. Since the work hardening rate was also increased, the uniform elongation was not significantly decreased by the addition of nitrogen. However, the local elongation was reduced drastically through the occurrence of intergranular brittle fracture even by a small amount of nitrogen addition. In the tensile-deformed pure Ti, many deformation twins and dislocations were observed. On the other hand, few deformation twins and a high density of planar dislocation arrays were observed in the high nitrogen alloys. The changes in deformation structure might have caused the reduction of local elongation in nitrogen added alloys because of the intergranular brittle fracture derived from the suppression of twinning deformation and the stress concentration at grain boundary due to piled-up dislocations in the planar array.

Original languageEnglish
Pages (from-to)949-954
Number of pages6
JournalNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
Volume72
Issue number12
DOIs
Publication statusPublished - Dec 1 2008

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Effect of nitrogen on tensile deformation behavior and development of deformation structure in titanium'. Together they form a unique fingerprint.

  • Cite this