Effect of S content in deposit on low-cycle fatigue properties of Ni film electroplated from sulfamate baths

Akira Kubota, Masato Takada, Tomonori Nakao, Hiroaki Nakano, Satoshi Oue, Tetsuya Akiyama, Hisaaki Fukushima, Ryuta Onodera

Research output: Contribution to journalArticle

8 Citations (Scopus)

Abstract

Nickel was electrodeposited from sulfamate baths containing various amounts of thiourea. The effect of S in the deposit on the fatigue properties of electroplated Ni was studied by low-cycle fatigue test and by the observation of the fractured surface of the deposit. The results obtained were as follows: (1) In the deposit of low S content (1.3×10-4 mass%), the low-cycle fatigue properties were able to be estimated by the tensile test on the basis of Manson's cogradient law. However, the result of tensile test was not applicable to the deposits of high S content (46×10-4 mass%) because of their poor fatigue properties. (2) The striation was recognized on the fracture surface of the deposit containing 1.3×10-4 mass% S, which suggested that transgranular fracture peculiar to the low-cycle fatigue occurred. On the contrary, the deposit of 46×10-4 mass% S was consisted of polycrystal colonies with the polygonal shape (several millimeters in size). Since the strength in colony boundary was lower than that in colony itself, the fracture proceeded along the colony boundary. (3) During annealing, S in the deposits diffused into the boundary between grains recrystallized. Therefore, the fracture might occur along the grain boundary embrittled by S.

Original languageEnglish
Pages (from-to)38-44
Number of pages7
JournalTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
Volume86
Issue number1
DOIs
Publication statusPublished - Jan 1 2000

Fingerprint

baths
Deposits
deposits
Fatigue of materials
cycles
tensile tests
Grain boundaries
Thiourea
fatigue tests
striation
Thioureas
thioureas
Polycrystals
polycrystals
sulfamic acid
Nickel
grain boundaries
nickel
Annealing
annealing

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

Cite this

Effect of S content in deposit on low-cycle fatigue properties of Ni film electroplated from sulfamate baths. / Kubota, Akira; Takada, Masato; Nakao, Tomonori; Nakano, Hiroaki; Oue, Satoshi; Akiyama, Tetsuya; Fukushima, Hisaaki; Onodera, Ryuta.

In: Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, Vol. 86, No. 1, 01.01.2000, p. 38-44.

Research output: Contribution to journalArticle

Kubota, Akira ; Takada, Masato ; Nakao, Tomonori ; Nakano, Hiroaki ; Oue, Satoshi ; Akiyama, Tetsuya ; Fukushima, Hisaaki ; Onodera, Ryuta. / Effect of S content in deposit on low-cycle fatigue properties of Ni film electroplated from sulfamate baths. In: Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan. 2000 ; Vol. 86, No. 1. pp. 38-44.
@article{245cfd7c568d4709a64dd5d2e80c7eb3,
title = "Effect of S content in deposit on low-cycle fatigue properties of Ni film electroplated from sulfamate baths",
abstract = "Nickel was electrodeposited from sulfamate baths containing various amounts of thiourea. The effect of S in the deposit on the fatigue properties of electroplated Ni was studied by low-cycle fatigue test and by the observation of the fractured surface of the deposit. The results obtained were as follows: (1) In the deposit of low S content (1.3×10-4 mass{\%}), the low-cycle fatigue properties were able to be estimated by the tensile test on the basis of Manson's cogradient law. However, the result of tensile test was not applicable to the deposits of high S content (46×10-4 mass{\%}) because of their poor fatigue properties. (2) The striation was recognized on the fracture surface of the deposit containing 1.3×10-4 mass{\%} S, which suggested that transgranular fracture peculiar to the low-cycle fatigue occurred. On the contrary, the deposit of 46×10-4 mass{\%} S was consisted of polycrystal colonies with the polygonal shape (several millimeters in size). Since the strength in colony boundary was lower than that in colony itself, the fracture proceeded along the colony boundary. (3) During annealing, S in the deposits diffused into the boundary between grains recrystallized. Therefore, the fracture might occur along the grain boundary embrittled by S.",
author = "Akira Kubota and Masato Takada and Tomonori Nakao and Hiroaki Nakano and Satoshi Oue and Tetsuya Akiyama and Hisaaki Fukushima and Ryuta Onodera",
year = "2000",
month = "1",
day = "1",
doi = "10.2355/tetsutohagane1955.86.1_38",
language = "English",
volume = "86",
pages = "38--44",
journal = "Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan",
issn = "0021-1575",
publisher = "一般社団法人 日本鉄鋼協会",
number = "1",

}

TY - JOUR

T1 - Effect of S content in deposit on low-cycle fatigue properties of Ni film electroplated from sulfamate baths

AU - Kubota, Akira

AU - Takada, Masato

AU - Nakao, Tomonori

AU - Nakano, Hiroaki

AU - Oue, Satoshi

AU - Akiyama, Tetsuya

AU - Fukushima, Hisaaki

AU - Onodera, Ryuta

PY - 2000/1/1

Y1 - 2000/1/1

N2 - Nickel was electrodeposited from sulfamate baths containing various amounts of thiourea. The effect of S in the deposit on the fatigue properties of electroplated Ni was studied by low-cycle fatigue test and by the observation of the fractured surface of the deposit. The results obtained were as follows: (1) In the deposit of low S content (1.3×10-4 mass%), the low-cycle fatigue properties were able to be estimated by the tensile test on the basis of Manson's cogradient law. However, the result of tensile test was not applicable to the deposits of high S content (46×10-4 mass%) because of their poor fatigue properties. (2) The striation was recognized on the fracture surface of the deposit containing 1.3×10-4 mass% S, which suggested that transgranular fracture peculiar to the low-cycle fatigue occurred. On the contrary, the deposit of 46×10-4 mass% S was consisted of polycrystal colonies with the polygonal shape (several millimeters in size). Since the strength in colony boundary was lower than that in colony itself, the fracture proceeded along the colony boundary. (3) During annealing, S in the deposits diffused into the boundary between grains recrystallized. Therefore, the fracture might occur along the grain boundary embrittled by S.

AB - Nickel was electrodeposited from sulfamate baths containing various amounts of thiourea. The effect of S in the deposit on the fatigue properties of electroplated Ni was studied by low-cycle fatigue test and by the observation of the fractured surface of the deposit. The results obtained were as follows: (1) In the deposit of low S content (1.3×10-4 mass%), the low-cycle fatigue properties were able to be estimated by the tensile test on the basis of Manson's cogradient law. However, the result of tensile test was not applicable to the deposits of high S content (46×10-4 mass%) because of their poor fatigue properties. (2) The striation was recognized on the fracture surface of the deposit containing 1.3×10-4 mass% S, which suggested that transgranular fracture peculiar to the low-cycle fatigue occurred. On the contrary, the deposit of 46×10-4 mass% S was consisted of polycrystal colonies with the polygonal shape (several millimeters in size). Since the strength in colony boundary was lower than that in colony itself, the fracture proceeded along the colony boundary. (3) During annealing, S in the deposits diffused into the boundary between grains recrystallized. Therefore, the fracture might occur along the grain boundary embrittled by S.

UR - http://www.scopus.com/inward/record.url?scp=0033887271&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0033887271&partnerID=8YFLogxK

U2 - 10.2355/tetsutohagane1955.86.1_38

DO - 10.2355/tetsutohagane1955.86.1_38

M3 - Article

AN - SCOPUS:0033887271

VL - 86

SP - 38

EP - 44

JO - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

JF - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

SN - 0021-1575

IS - 1

ER -