Effect of statistical distribution of iron powder size on fatigue strength of powder metals

Hisao Matsunaga, Owe Mårs, Bengt Johannesson, Yukitaka Murakami

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

Fatigue properties of two kinds of ferrous powder metals, which were produced from partially prealloyed iron powders and whose densities are 7.10 g/cm3 and 7.35 g/cm3, were investigated by tension-compression fatigue test. Main fatigue cracks did not initiate from pores but from slip bands in soft Fe particles in both these materials. The crack nucleated at the maximum Fe particle behaved as a defect larger than the maximum pore and accordingly the maximum size of the Fe particle existing on specimen surface was the crucial factor determining the fatigue strength. In order to confirm this fact more exactly, the maximum Fe particle size was evaluated by the statistics of extremes, and on the other hand an artificial hole with various sizes was introduced onto the specimen surface and the influence of the hole was investigated. The prediction of the maximum size of Fe particle by the statistics of extremes was in good agreement with the critical size of the artificial hole which was detrimental to fatigue strength. These facts explain that the difference in the fatigue strength between two materials was not caused by the difference in densities, i.e. pores, but by the strength properties of the microstructures such as Vickers hardness which was measured in details from the core to boundaries of grains.

Original languageEnglish
Pages (from-to)1101-1106
Number of pages6
JournalZairyo/Journal of the Society of Materials Science, Japan
Volume48
Issue number10
DOIs
Publication statusPublished - Jan 1 1999

Fingerprint

metal powder
Iron powder
Powder metals
statistical distributions
iron
Statistics
Fatigue of materials
porosity
Vickers hardness
cracks
statistics
Compaction
Particle size
fatigue tests
Cracks
edge dislocations
Defects
Microstructure
Fatigue strength
microstructure

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Effect of statistical distribution of iron powder size on fatigue strength of powder metals. / Matsunaga, Hisao; Mårs, Owe; Johannesson, Bengt; Murakami, Yukitaka.

In: Zairyo/Journal of the Society of Materials Science, Japan, Vol. 48, No. 10, 01.01.1999, p. 1101-1106.

Research output: Contribution to journalArticle

@article{b3b36878700645e3947e64b8bcd96a2e,
title = "Effect of statistical distribution of iron powder size on fatigue strength of powder metals",
abstract = "Fatigue properties of two kinds of ferrous powder metals, which were produced from partially prealloyed iron powders and whose densities are 7.10 g/cm3 and 7.35 g/cm3, were investigated by tension-compression fatigue test. Main fatigue cracks did not initiate from pores but from slip bands in soft Fe particles in both these materials. The crack nucleated at the maximum Fe particle behaved as a defect larger than the maximum pore and accordingly the maximum size of the Fe particle existing on specimen surface was the crucial factor determining the fatigue strength. In order to confirm this fact more exactly, the maximum Fe particle size was evaluated by the statistics of extremes, and on the other hand an artificial hole with various sizes was introduced onto the specimen surface and the influence of the hole was investigated. The prediction of the maximum size of Fe particle by the statistics of extremes was in good agreement with the critical size of the artificial hole which was detrimental to fatigue strength. These facts explain that the difference in the fatigue strength between two materials was not caused by the difference in densities, i.e. pores, but by the strength properties of the microstructures such as Vickers hardness which was measured in details from the core to boundaries of grains.",
author = "Hisao Matsunaga and Owe M{\aa}rs and Bengt Johannesson and Yukitaka Murakami",
year = "1999",
month = "1",
day = "1",
doi = "10.2472/jsms.48.1101",
language = "English",
volume = "48",
pages = "1101--1106",
journal = "Zairyo/Journal of the Society of Materials Science, Japan",
issn = "0514-5163",
publisher = "公益社団法人 日本材料学会",
number = "10",

}

TY - JOUR

T1 - Effect of statistical distribution of iron powder size on fatigue strength of powder metals

AU - Matsunaga, Hisao

AU - Mårs, Owe

AU - Johannesson, Bengt

AU - Murakami, Yukitaka

PY - 1999/1/1

Y1 - 1999/1/1

N2 - Fatigue properties of two kinds of ferrous powder metals, which were produced from partially prealloyed iron powders and whose densities are 7.10 g/cm3 and 7.35 g/cm3, were investigated by tension-compression fatigue test. Main fatigue cracks did not initiate from pores but from slip bands in soft Fe particles in both these materials. The crack nucleated at the maximum Fe particle behaved as a defect larger than the maximum pore and accordingly the maximum size of the Fe particle existing on specimen surface was the crucial factor determining the fatigue strength. In order to confirm this fact more exactly, the maximum Fe particle size was evaluated by the statistics of extremes, and on the other hand an artificial hole with various sizes was introduced onto the specimen surface and the influence of the hole was investigated. The prediction of the maximum size of Fe particle by the statistics of extremes was in good agreement with the critical size of the artificial hole which was detrimental to fatigue strength. These facts explain that the difference in the fatigue strength between two materials was not caused by the difference in densities, i.e. pores, but by the strength properties of the microstructures such as Vickers hardness which was measured in details from the core to boundaries of grains.

AB - Fatigue properties of two kinds of ferrous powder metals, which were produced from partially prealloyed iron powders and whose densities are 7.10 g/cm3 and 7.35 g/cm3, were investigated by tension-compression fatigue test. Main fatigue cracks did not initiate from pores but from slip bands in soft Fe particles in both these materials. The crack nucleated at the maximum Fe particle behaved as a defect larger than the maximum pore and accordingly the maximum size of the Fe particle existing on specimen surface was the crucial factor determining the fatigue strength. In order to confirm this fact more exactly, the maximum Fe particle size was evaluated by the statistics of extremes, and on the other hand an artificial hole with various sizes was introduced onto the specimen surface and the influence of the hole was investigated. The prediction of the maximum size of Fe particle by the statistics of extremes was in good agreement with the critical size of the artificial hole which was detrimental to fatigue strength. These facts explain that the difference in the fatigue strength between two materials was not caused by the difference in densities, i.e. pores, but by the strength properties of the microstructures such as Vickers hardness which was measured in details from the core to boundaries of grains.

UR - http://www.scopus.com/inward/record.url?scp=0033207385&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0033207385&partnerID=8YFLogxK

U2 - 10.2472/jsms.48.1101

DO - 10.2472/jsms.48.1101

M3 - Article

AN - SCOPUS:0033207385

VL - 48

SP - 1101

EP - 1106

JO - Zairyo/Journal of the Society of Materials Science, Japan

JF - Zairyo/Journal of the Society of Materials Science, Japan

SN - 0514-5163

IS - 10

ER -