Effects of sintering temperature over 1,300°C on the physical and compositional properties of porous hydroxyapatite foam

Melvin L. Munar, Koh Ichi Udoh, Kunio Ishikawa, Shigeki Matsuya, Masaharu Nakagawa

Research output: Contribution to journalArticle

35 Citations (Scopus)

Abstract

Porous hydroxyapatite (HAP) foam permits three-dimensional (3D) structure with fully interconnecting pores as well as excellent tissue response and good osteoconductivity. It is therefore thought to be a good candidate as scaffold material for bone regeneration and as a synthetic bone substitute material. To fabricate better porous HAP foam, improved physical and structural properties as well as higher osteoconductivity are desired. In the present study, the effects of sintering temperature on the physical and compositional properties of porous HAP foam were evaluated by employing high sintering temperature starting at 1,300°C up to 1,550°C. The mechanical strength of porous HAP foam increased with sintering temperature to reach the maximum value at l,525°C, then decreased slightly when sintering temperature was further increased to 1,550°C. Alpha tricalcium phosphate (α-TCP) was formed, and thus the porous HAP foam became biphasic calcium phosphate. Biphasic calcium phosphate consisting of both α-TCP and HAP had been reported to show higher osteoconductivity than HAP alone. We therefore recommend 1,500-1,550°C as the sintering temperature for porous HAP foam since this condition provided the most desirable physical properties with biphasic calcium phosphate composition.

Original languageEnglish
Pages (from-to)51-58
Number of pages8
JournalDental Materials Journal
Volume25
Issue number1
DOIs
Publication statusPublished - Mar 1 2006

Fingerprint

Durapatite
Hydroxyapatite
Foams
Sintering
Temperature
Calcium phosphate
Bone
Physical properties
Bone Substitutes
Bone Regeneration
Scaffolds
Strength of materials
Structural properties
Phosphates
Tissue
Chemical analysis
hydroxyapatite-beta tricalcium phosphate

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Dentistry(all)

Cite this

Effects of sintering temperature over 1,300°C on the physical and compositional properties of porous hydroxyapatite foam. / Munar, Melvin L.; Udoh, Koh Ichi; Ishikawa, Kunio; Matsuya, Shigeki; Nakagawa, Masaharu.

In: Dental Materials Journal, Vol. 25, No. 1, 01.03.2006, p. 51-58.

Research output: Contribution to journalArticle

@article{03c35faf295441e7ad8df20905088643,
title = "Effects of sintering temperature over 1,300°C on the physical and compositional properties of porous hydroxyapatite foam",
abstract = "Porous hydroxyapatite (HAP) foam permits three-dimensional (3D) structure with fully interconnecting pores as well as excellent tissue response and good osteoconductivity. It is therefore thought to be a good candidate as scaffold material for bone regeneration and as a synthetic bone substitute material. To fabricate better porous HAP foam, improved physical and structural properties as well as higher osteoconductivity are desired. In the present study, the effects of sintering temperature on the physical and compositional properties of porous HAP foam were evaluated by employing high sintering temperature starting at 1,300°C up to 1,550°C. The mechanical strength of porous HAP foam increased with sintering temperature to reach the maximum value at l,525°C, then decreased slightly when sintering temperature was further increased to 1,550°C. Alpha tricalcium phosphate (α-TCP) was formed, and thus the porous HAP foam became biphasic calcium phosphate. Biphasic calcium phosphate consisting of both α-TCP and HAP had been reported to show higher osteoconductivity than HAP alone. We therefore recommend 1,500-1,550°C as the sintering temperature for porous HAP foam since this condition provided the most desirable physical properties with biphasic calcium phosphate composition.",
author = "Munar, {Melvin L.} and Udoh, {Koh Ichi} and Kunio Ishikawa and Shigeki Matsuya and Masaharu Nakagawa",
year = "2006",
month = "3",
day = "1",
doi = "10.4012/dmj.25.51",
language = "English",
volume = "25",
pages = "51--58",
journal = "Dental Materials Journal",
issn = "0287-4547",
publisher = "Japanese Society for Dental Materials and Devices",
number = "1",

}

TY - JOUR

T1 - Effects of sintering temperature over 1,300°C on the physical and compositional properties of porous hydroxyapatite foam

AU - Munar, Melvin L.

AU - Udoh, Koh Ichi

AU - Ishikawa, Kunio

AU - Matsuya, Shigeki

AU - Nakagawa, Masaharu

PY - 2006/3/1

Y1 - 2006/3/1

N2 - Porous hydroxyapatite (HAP) foam permits three-dimensional (3D) structure with fully interconnecting pores as well as excellent tissue response and good osteoconductivity. It is therefore thought to be a good candidate as scaffold material for bone regeneration and as a synthetic bone substitute material. To fabricate better porous HAP foam, improved physical and structural properties as well as higher osteoconductivity are desired. In the present study, the effects of sintering temperature on the physical and compositional properties of porous HAP foam were evaluated by employing high sintering temperature starting at 1,300°C up to 1,550°C. The mechanical strength of porous HAP foam increased with sintering temperature to reach the maximum value at l,525°C, then decreased slightly when sintering temperature was further increased to 1,550°C. Alpha tricalcium phosphate (α-TCP) was formed, and thus the porous HAP foam became biphasic calcium phosphate. Biphasic calcium phosphate consisting of both α-TCP and HAP had been reported to show higher osteoconductivity than HAP alone. We therefore recommend 1,500-1,550°C as the sintering temperature for porous HAP foam since this condition provided the most desirable physical properties with biphasic calcium phosphate composition.

AB - Porous hydroxyapatite (HAP) foam permits three-dimensional (3D) structure with fully interconnecting pores as well as excellent tissue response and good osteoconductivity. It is therefore thought to be a good candidate as scaffold material for bone regeneration and as a synthetic bone substitute material. To fabricate better porous HAP foam, improved physical and structural properties as well as higher osteoconductivity are desired. In the present study, the effects of sintering temperature on the physical and compositional properties of porous HAP foam were evaluated by employing high sintering temperature starting at 1,300°C up to 1,550°C. The mechanical strength of porous HAP foam increased with sintering temperature to reach the maximum value at l,525°C, then decreased slightly when sintering temperature was further increased to 1,550°C. Alpha tricalcium phosphate (α-TCP) was formed, and thus the porous HAP foam became biphasic calcium phosphate. Biphasic calcium phosphate consisting of both α-TCP and HAP had been reported to show higher osteoconductivity than HAP alone. We therefore recommend 1,500-1,550°C as the sintering temperature for porous HAP foam since this condition provided the most desirable physical properties with biphasic calcium phosphate composition.

UR - http://www.scopus.com/inward/record.url?scp=33745240367&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33745240367&partnerID=8YFLogxK

U2 - 10.4012/dmj.25.51

DO - 10.4012/dmj.25.51

M3 - Article

VL - 25

SP - 51

EP - 58

JO - Dental Materials Journal

JF - Dental Materials Journal

SN - 0287-4547

IS - 1

ER -