Electron spin resonance studies of gamma-irradiation damage in simulated nuclear waste glass

Yaohiro Inagaki, Hirotaka Furuya, Tsuneomi Kikuchi, Kazuya Idemitsu

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

The effects of r-irradiation on a simulated nuclear waste glass were studied by electron spin resonance spectroscopy (ESR), and were compared with the results on silica glass and Pyrex glass. Three kinds of glasses were /-irradiated up to the dose of 1.22 MGy and the ESR spectra were obtained. The intensity of ESR spectra were obtained as a function of irradiation dose and annealing temperature. The spectrum of the waste glass was characteristic of two typical peaks, Peak 1 was the strong resonance at 0=4.3 showing the existence of four coordinated Fe3+ and Peak 2 was the weak and broad resonance at 3=2.0 showing the existence of six coordinated Fe3+. The ESR spectra of the waste glass before and after r-irradiation were almost overlapped and a little difference only in the intensity was observed. While in silaca glass and Pyrex glass, the peaks from E'r center and boron-oxygen hole center (BOHC) were observed to arise after irradiation. The absolute intensity of Peaks 1 and 2 described above changed in complicated way depending on the dose. The result suggests oxidation or reduction of iron takes place in the waste glass depending on the dose. The isochronal annealing of irradiated glasses shows most of f-ray- induced damages in the waste glass are restored even at room temperature, although most of the damages in silica glass and Pyrex glass are disappeared at the temperature from 550 to 600 K. The results show that the waste glass with a few weight percent of iron is resistent to radiation than other commercial glasses.

Original languageEnglish
Pages (from-to)314-320
Number of pages7
Journaljournal of nuclear science and technology
Volume28
Issue number4
DOIs
Publication statusPublished - Jan 1 1991

Fingerprint

radioactive wastes
Radioactive wastes
Paramagnetic resonance
electron paramagnetic resonance
Irradiation
damage
Glass
irradiation
glass
Electron spin resonance spectroscopy
borosilicate glass
dosage
silica glass
Fused silica
spectroscopy
Annealing
Iron
iron
annealing
Temperature

All Science Journal Classification (ASJC) codes

  • Nuclear and High Energy Physics
  • Nuclear Energy and Engineering

Cite this

Electron spin resonance studies of gamma-irradiation damage in simulated nuclear waste glass. / Inagaki, Yaohiro; Furuya, Hirotaka; Kikuchi, Tsuneomi; Idemitsu, Kazuya.

In: journal of nuclear science and technology, Vol. 28, No. 4, 01.01.1991, p. 314-320.

Research output: Contribution to journalArticle

@article{f03bb9df4540425e85d01c25f8c66f6d,
title = "Electron spin resonance studies of gamma-irradiation damage in simulated nuclear waste glass",
abstract = "The effects of r-irradiation on a simulated nuclear waste glass were studied by electron spin resonance spectroscopy (ESR), and were compared with the results on silica glass and Pyrex glass. Three kinds of glasses were /-irradiated up to the dose of 1.22 MGy and the ESR spectra were obtained. The intensity of ESR spectra were obtained as a function of irradiation dose and annealing temperature. The spectrum of the waste glass was characteristic of two typical peaks, Peak 1 was the strong resonance at 0=4.3 showing the existence of four coordinated Fe3+ and Peak 2 was the weak and broad resonance at 3=2.0 showing the existence of six coordinated Fe3+. The ESR spectra of the waste glass before and after r-irradiation were almost overlapped and a little difference only in the intensity was observed. While in silaca glass and Pyrex glass, the peaks from E'r center and boron-oxygen hole center (BOHC) were observed to arise after irradiation. The absolute intensity of Peaks 1 and 2 described above changed in complicated way depending on the dose. The result suggests oxidation or reduction of iron takes place in the waste glass depending on the dose. The isochronal annealing of irradiated glasses shows most of f-ray- induced damages in the waste glass are restored even at room temperature, although most of the damages in silica glass and Pyrex glass are disappeared at the temperature from 550 to 600 K. The results show that the waste glass with a few weight percent of iron is resistent to radiation than other commercial glasses.",
author = "Yaohiro Inagaki and Hirotaka Furuya and Tsuneomi Kikuchi and Kazuya Idemitsu",
year = "1991",
month = "1",
day = "1",
doi = "10.1080/18811248.1991.9731361",
language = "English",
volume = "28",
pages = "314--320",
journal = "Journal of Nuclear Science and Technology",
issn = "0022-3131",
publisher = "Atomic Energy Society of Japan",
number = "4",

}

TY - JOUR

T1 - Electron spin resonance studies of gamma-irradiation damage in simulated nuclear waste glass

AU - Inagaki, Yaohiro

AU - Furuya, Hirotaka

AU - Kikuchi, Tsuneomi

AU - Idemitsu, Kazuya

PY - 1991/1/1

Y1 - 1991/1/1

N2 - The effects of r-irradiation on a simulated nuclear waste glass were studied by electron spin resonance spectroscopy (ESR), and were compared with the results on silica glass and Pyrex glass. Three kinds of glasses were /-irradiated up to the dose of 1.22 MGy and the ESR spectra were obtained. The intensity of ESR spectra were obtained as a function of irradiation dose and annealing temperature. The spectrum of the waste glass was characteristic of two typical peaks, Peak 1 was the strong resonance at 0=4.3 showing the existence of four coordinated Fe3+ and Peak 2 was the weak and broad resonance at 3=2.0 showing the existence of six coordinated Fe3+. The ESR spectra of the waste glass before and after r-irradiation were almost overlapped and a little difference only in the intensity was observed. While in silaca glass and Pyrex glass, the peaks from E'r center and boron-oxygen hole center (BOHC) were observed to arise after irradiation. The absolute intensity of Peaks 1 and 2 described above changed in complicated way depending on the dose. The result suggests oxidation or reduction of iron takes place in the waste glass depending on the dose. The isochronal annealing of irradiated glasses shows most of f-ray- induced damages in the waste glass are restored even at room temperature, although most of the damages in silica glass and Pyrex glass are disappeared at the temperature from 550 to 600 K. The results show that the waste glass with a few weight percent of iron is resistent to radiation than other commercial glasses.

AB - The effects of r-irradiation on a simulated nuclear waste glass were studied by electron spin resonance spectroscopy (ESR), and were compared with the results on silica glass and Pyrex glass. Three kinds of glasses were /-irradiated up to the dose of 1.22 MGy and the ESR spectra were obtained. The intensity of ESR spectra were obtained as a function of irradiation dose and annealing temperature. The spectrum of the waste glass was characteristic of two typical peaks, Peak 1 was the strong resonance at 0=4.3 showing the existence of four coordinated Fe3+ and Peak 2 was the weak and broad resonance at 3=2.0 showing the existence of six coordinated Fe3+. The ESR spectra of the waste glass before and after r-irradiation were almost overlapped and a little difference only in the intensity was observed. While in silaca glass and Pyrex glass, the peaks from E'r center and boron-oxygen hole center (BOHC) were observed to arise after irradiation. The absolute intensity of Peaks 1 and 2 described above changed in complicated way depending on the dose. The result suggests oxidation or reduction of iron takes place in the waste glass depending on the dose. The isochronal annealing of irradiated glasses shows most of f-ray- induced damages in the waste glass are restored even at room temperature, although most of the damages in silica glass and Pyrex glass are disappeared at the temperature from 550 to 600 K. The results show that the waste glass with a few weight percent of iron is resistent to radiation than other commercial glasses.

UR - http://www.scopus.com/inward/record.url?scp=0026138392&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0026138392&partnerID=8YFLogxK

U2 - 10.1080/18811248.1991.9731361

DO - 10.1080/18811248.1991.9731361

M3 - Article

VL - 28

SP - 314

EP - 320

JO - Journal of Nuclear Science and Technology

JF - Journal of Nuclear Science and Technology

SN - 0022-3131

IS - 4

ER -