Evaluation of specific surface area and pore size distribution of la Ni 0.6 Fe 0.4 O 3 ceramics prepared using Pechini method by N 2 adsorption method-optimization of sintering temperature as cathode material of solid oxide fuel cells

Eiki Niwa, Chie Uematsu, Takuya Hashimoto

Research output: Contribution to journalArticlepeer-review

10 Citations (Scopus)

Abstract

Sintering temperature dependences of specific surface area, pore size distribution, and pore volume of LaNi0.6Fe0.4O3 ceramics prepared using the Pechini method have been evaluated from the adsorption isotherms of N2 gas at -195.8°C. The specific surface area decreased almost linearly with increasing sintering temperature showing that preparation of the ceramic specimens with controlled surface area is possible by sintering temperature. The pore size distribution, evaluated by BJH method, showed two peaks around 2.5 and 250 nm with narrow FWHM for the specimen sintered at 900°C. Although both the peaks were maintained in the specimens sintered at 1000°C and 1100°C, their intensity decreased with increasing sintering temperature, indicating decrease of pore volume. It has been revealed that sintering below 1100°C is necessary to prepare LaNi 0.6Fe0.4O3 ceramics with pore volume maintained, which is suitable for SOFC cathode material.

Original languageEnglish
Pages (from-to)3802-3806
Number of pages5
JournalJournal of the American Ceramic Society
Volume95
Issue number12
DOIs
Publication statusPublished - Dec 2012
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Evaluation of specific surface area and pore size distribution of la Ni <sub>0.6</sub> Fe <sub>0.4</sub> O <sub>3</sub> ceramics prepared using Pechini method by N <sub>2</sub> adsorption method-optimization of sintering temperature as cathode material of solid oxide fuel cells'. Together they form a unique fingerprint.

Cite this