Examination of tensile deformation and void nucleation behaviors of duplex stainless steel using nano-indentation hardness test

Masatoshi Aramaki, Satoshi Uchida, Kyono Yasuda, Makoto Oikawa, Osamu Furukimi

Research output: Contribution to journalArticle

4 Citations (Scopus)

Abstract

The plastic deformation behavior in a uniaxial tensile test was examined by applying the nano-indentation hardness test to the ferrite-austenite duplex stainless steel. Each phase revealed the same hardness and a different work hardening ratio. The effect of the hardness difference in each phase on the void nucleation process was investigated by means of EBSD analysis. From the EBSD analysis, deformation twinning and deformation-induced martensitic transformation were observed in the austenite phase near the fracture surface. The hardness of austenite rose to a higher degree than that of ferrite, and showed an extremely-high value due to martensitic transformation. The void appeared mainly at the interface between the martensite induced by deformation and the ferrite phases. Thus the void nucleation was enhanced by the martensitic transformation which occurred at the location of higher equivalent strain of 1.5.

Original languageEnglish
Pages (from-to)1261-1266
Number of pages6
JournalTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
Volume100
Issue number10
DOIs
Publication statusPublished - Jan 1 2014

Fingerprint

hardness tests
tensile deformation
Stainless Steel
martensitic transformation
Nanoindentation
nanoindentation
austenite
voids
stainless steels
ferrites
Martensitic transformations
Nucleation
hardness
Stainless steel
examination
Hardness
nucleation
Austenite
Ferrite
work hardening

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

Cite this

Examination of tensile deformation and void nucleation behaviors of duplex stainless steel using nano-indentation hardness test. / Aramaki, Masatoshi; Uchida, Satoshi; Yasuda, Kyono; Oikawa, Makoto; Furukimi, Osamu.

In: Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, Vol. 100, No. 10, 01.01.2014, p. 1261-1266.

Research output: Contribution to journalArticle

@article{d5b6670818ea4d70bf366423bd57230f,
title = "Examination of tensile deformation and void nucleation behaviors of duplex stainless steel using nano-indentation hardness test",
abstract = "The plastic deformation behavior in a uniaxial tensile test was examined by applying the nano-indentation hardness test to the ferrite-austenite duplex stainless steel. Each phase revealed the same hardness and a different work hardening ratio. The effect of the hardness difference in each phase on the void nucleation process was investigated by means of EBSD analysis. From the EBSD analysis, deformation twinning and deformation-induced martensitic transformation were observed in the austenite phase near the fracture surface. The hardness of austenite rose to a higher degree than that of ferrite, and showed an extremely-high value due to martensitic transformation. The void appeared mainly at the interface between the martensite induced by deformation and the ferrite phases. Thus the void nucleation was enhanced by the martensitic transformation which occurred at the location of higher equivalent strain of 1.5.",
author = "Masatoshi Aramaki and Satoshi Uchida and Kyono Yasuda and Makoto Oikawa and Osamu Furukimi",
year = "2014",
month = "1",
day = "1",
doi = "10.2355/tetsutohagane.100.1261",
language = "English",
volume = "100",
pages = "1261--1266",
journal = "Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan",
issn = "0021-1575",
publisher = "一般社団法人 日本鉄鋼協会",
number = "10",

}

TY - JOUR

T1 - Examination of tensile deformation and void nucleation behaviors of duplex stainless steel using nano-indentation hardness test

AU - Aramaki, Masatoshi

AU - Uchida, Satoshi

AU - Yasuda, Kyono

AU - Oikawa, Makoto

AU - Furukimi, Osamu

PY - 2014/1/1

Y1 - 2014/1/1

N2 - The plastic deformation behavior in a uniaxial tensile test was examined by applying the nano-indentation hardness test to the ferrite-austenite duplex stainless steel. Each phase revealed the same hardness and a different work hardening ratio. The effect of the hardness difference in each phase on the void nucleation process was investigated by means of EBSD analysis. From the EBSD analysis, deformation twinning and deformation-induced martensitic transformation were observed in the austenite phase near the fracture surface. The hardness of austenite rose to a higher degree than that of ferrite, and showed an extremely-high value due to martensitic transformation. The void appeared mainly at the interface between the martensite induced by deformation and the ferrite phases. Thus the void nucleation was enhanced by the martensitic transformation which occurred at the location of higher equivalent strain of 1.5.

AB - The plastic deformation behavior in a uniaxial tensile test was examined by applying the nano-indentation hardness test to the ferrite-austenite duplex stainless steel. Each phase revealed the same hardness and a different work hardening ratio. The effect of the hardness difference in each phase on the void nucleation process was investigated by means of EBSD analysis. From the EBSD analysis, deformation twinning and deformation-induced martensitic transformation were observed in the austenite phase near the fracture surface. The hardness of austenite rose to a higher degree than that of ferrite, and showed an extremely-high value due to martensitic transformation. The void appeared mainly at the interface between the martensite induced by deformation and the ferrite phases. Thus the void nucleation was enhanced by the martensitic transformation which occurred at the location of higher equivalent strain of 1.5.

UR - http://www.scopus.com/inward/record.url?scp=84908121637&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84908121637&partnerID=8YFLogxK

U2 - 10.2355/tetsutohagane.100.1261

DO - 10.2355/tetsutohagane.100.1261

M3 - Article

AN - SCOPUS:84908121637

VL - 100

SP - 1261

EP - 1266

JO - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

JF - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

SN - 0021-1575

IS - 10

ER -