Fabrication of porous carbonate apatite granules using microfiber and its histological evaluations in rabbit calvarial bone defects

Kazuya Akita, Naoyuki Fukuda, Kumiko Kamada, Keiko Kudoh, Naito Kurio, Kanji Tsuru, Kunio Ishikawa, Youji Miyamoto

Research output: Contribution to journalArticle

Abstract

Carbonate apatite (CO3Ap) granules are known to show good osteoconductivity and replaced to new bone. On the other hand, it is well known that a porous structure allows bone tissue to penetrate its pores, and the optimal pore size for bone ingrowth is dependent on the composition and structure of the scaffold material. Therefore, the aim of this study was to fabricate various porous CO3Ap granules through a two-step dissolution–precipitation reaction using CaSO4 as a precursor and 30-, 50-, 120-, and 205-μm diameter microfibers as porogen and to find the optimal pore size of CO3Ap. Porous CO3Ap granules were successfully fabricated with pore size 8.2–18.7% smaller than the size of the original fiber porogen. Two weeks after the reconstruction of rabbit calvarial bone defects using porous CO3Ap granules, the largest amount of mature bone was seen to be formed inside the pores of CO3Ap (120) [porous CO3Ap granules made using 120-μm microfiber] followed by CO3Ap (50) and CO3Ap (30). At 4 and 8 weeks, no statistically significant difference was observed based on the pore size, even though largest amount of mature bone was formed in case of CO3Ap (120). It is concluded, therefore, that the optimal pore size of the CO3Ap is that of CO3Ap (120), which is 85 μm.

Original languageEnglish
Pages (from-to)709-721
Number of pages13
JournalJournal of Biomedical Materials Research - Part A
Volume108
Issue number3
DOIs
Publication statusPublished - Mar 1 2020

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Biomaterials
  • Biomedical Engineering
  • Metals and Alloys

Fingerprint Dive into the research topics of 'Fabrication of porous carbonate apatite granules using microfiber and its histological evaluations in rabbit calvarial bone defects'. Together they form a unique fingerprint.

  • Cite this