The fatigue properties of a nickel-base superalloy, Inconel 718, in long-life region up to 10<SUP>8</SUP> cycles were investigated under rotating bending at room temperature and elevated temperature of 300°C, 500°C and 600°C. S-N curves at 500°C and 600°C showed the stepwise shapes, though those in cases of room temperature and 300°C were the conventional one-step ones. All the fractures originated from the specimen surface at room temperature and 300°C, while the internal fractures occurred in long-life region beyond 10<SUP>7</SUP> cycles and the surface fractures at the stress levels over the horizontal line of S-N curves corresponding to the fatigue limit for the surface fracture at 500°C and 600°C. Intergranular crackings were observed at the origin of internal fracture.
|Translated title of the contribution||Fatigue Properties of Ni-Base Superalloy in Long Life Region at Elevated Temperature|
|Number of pages||6|
|Journal||Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A|
|Publication status||Published - Aug 25 2002|
皮籠石紀雄, 陳強, 大坪謙一, 燕怒, 近藤英二, & 王清遠 (2002). Ni基超合金の長寿命域における中高温疲労特性. Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 68(672), 1192-1197. https://doi.org/10.1299/kikaia.68.1192