Formation of mesophase spheres from a coal tar pitch upon heating and subsequent cooling observed by an in situ 1H-NMR

R. Moriyama, H. Kumagai, Hayashi Jun-Ichiro, C. Yamaguchi, J. Mondori, H. Matsui, T. Chiba

Research output: Contribution to journalArticle

32 Citations (Scopus)

Abstract

Coal tar pitch was heated at a rate of 10 K/min up to 723 K in an atmospheric flow of nitrogen gas, soaked at the temperature for time, tH, ranging from 0 to 480 min. A microscopic observation revealed that soaking for tH shorter than 120 min produced dispersed mesophase spheres, while longer soaking resulted in a flow-textured mesophase due to a progress of coalescence of the spheres. Diameter and yield of the dispersed spheres depended on the rate of cooling, suggesting that the spheres formed upon cooling. In situ proton nuclear magnetic resonance (1H-NMR) detected three components, G1, G2 and W having different transverse magnetization decays, in the pitch upon soaking. Magnetization decays of G1 and W agreed well with those of meso-carbon microbeads (MCMB) and fully fused isotropic pitch, respectively. When tH was shorter than 60 min, no G1 was detected while spheres were observed in the pitch after cooling, confirming mesophase formation upon cooling after soaking. It was also found that the formation of spheres upon cooling accompanies the complete conversion of G2 into G1 and that the G1 formed hardly fuses while reheated to 723 K.

Original languageEnglish
Pages (from-to)749-758
Number of pages10
JournalCarbon
Volume38
Issue number5
DOIs
Publication statusPublished - Jan 1 2000
Externally publishedYes

Fingerprint

Coal Tar
Coal tar
Nuclear magnetic resonance
Cooling
Heating
Magnetization
Electric fuses
Coalescence
Nitrogen
Carbon
Gases

All Science Journal Classification (ASJC) codes

  • Chemistry(all)

Cite this

Formation of mesophase spheres from a coal tar pitch upon heating and subsequent cooling observed by an in situ 1H-NMR. / Moriyama, R.; Kumagai, H.; Jun-Ichiro, Hayashi; Yamaguchi, C.; Mondori, J.; Matsui, H.; Chiba, T.

In: Carbon, Vol. 38, No. 5, 01.01.2000, p. 749-758.

Research output: Contribution to journalArticle

Moriyama, R. ; Kumagai, H. ; Jun-Ichiro, Hayashi ; Yamaguchi, C. ; Mondori, J. ; Matsui, H. ; Chiba, T. / Formation of mesophase spheres from a coal tar pitch upon heating and subsequent cooling observed by an in situ 1H-NMR. In: Carbon. 2000 ; Vol. 38, No. 5. pp. 749-758.
@article{39ada9ed4b924485b8b320e57a5eb8b0,
title = "Formation of mesophase spheres from a coal tar pitch upon heating and subsequent cooling observed by an in situ 1H-NMR",
abstract = "Coal tar pitch was heated at a rate of 10 K/min up to 723 K in an atmospheric flow of nitrogen gas, soaked at the temperature for time, tH, ranging from 0 to 480 min. A microscopic observation revealed that soaking for tH shorter than 120 min produced dispersed mesophase spheres, while longer soaking resulted in a flow-textured mesophase due to a progress of coalescence of the spheres. Diameter and yield of the dispersed spheres depended on the rate of cooling, suggesting that the spheres formed upon cooling. In situ proton nuclear magnetic resonance (1H-NMR) detected three components, G1, G2 and W having different transverse magnetization decays, in the pitch upon soaking. Magnetization decays of G1 and W agreed well with those of meso-carbon microbeads (MCMB) and fully fused isotropic pitch, respectively. When tH was shorter than 60 min, no G1 was detected while spheres were observed in the pitch after cooling, confirming mesophase formation upon cooling after soaking. It was also found that the formation of spheres upon cooling accompanies the complete conversion of G2 into G1 and that the G1 formed hardly fuses while reheated to 723 K.",
author = "R. Moriyama and H. Kumagai and Hayashi Jun-Ichiro and C. Yamaguchi and J. Mondori and H. Matsui and T. Chiba",
year = "2000",
month = "1",
day = "1",
doi = "10.1016/S0008-6223(99)00152-9",
language = "English",
volume = "38",
pages = "749--758",
journal = "Carbon",
issn = "0008-6223",
publisher = "Elsevier Limited",
number = "5",

}

TY - JOUR

T1 - Formation of mesophase spheres from a coal tar pitch upon heating and subsequent cooling observed by an in situ 1H-NMR

AU - Moriyama, R.

AU - Kumagai, H.

AU - Jun-Ichiro, Hayashi

AU - Yamaguchi, C.

AU - Mondori, J.

AU - Matsui, H.

AU - Chiba, T.

PY - 2000/1/1

Y1 - 2000/1/1

N2 - Coal tar pitch was heated at a rate of 10 K/min up to 723 K in an atmospheric flow of nitrogen gas, soaked at the temperature for time, tH, ranging from 0 to 480 min. A microscopic observation revealed that soaking for tH shorter than 120 min produced dispersed mesophase spheres, while longer soaking resulted in a flow-textured mesophase due to a progress of coalescence of the spheres. Diameter and yield of the dispersed spheres depended on the rate of cooling, suggesting that the spheres formed upon cooling. In situ proton nuclear magnetic resonance (1H-NMR) detected three components, G1, G2 and W having different transverse magnetization decays, in the pitch upon soaking. Magnetization decays of G1 and W agreed well with those of meso-carbon microbeads (MCMB) and fully fused isotropic pitch, respectively. When tH was shorter than 60 min, no G1 was detected while spheres were observed in the pitch after cooling, confirming mesophase formation upon cooling after soaking. It was also found that the formation of spheres upon cooling accompanies the complete conversion of G2 into G1 and that the G1 formed hardly fuses while reheated to 723 K.

AB - Coal tar pitch was heated at a rate of 10 K/min up to 723 K in an atmospheric flow of nitrogen gas, soaked at the temperature for time, tH, ranging from 0 to 480 min. A microscopic observation revealed that soaking for tH shorter than 120 min produced dispersed mesophase spheres, while longer soaking resulted in a flow-textured mesophase due to a progress of coalescence of the spheres. Diameter and yield of the dispersed spheres depended on the rate of cooling, suggesting that the spheres formed upon cooling. In situ proton nuclear magnetic resonance (1H-NMR) detected three components, G1, G2 and W having different transverse magnetization decays, in the pitch upon soaking. Magnetization decays of G1 and W agreed well with those of meso-carbon microbeads (MCMB) and fully fused isotropic pitch, respectively. When tH was shorter than 60 min, no G1 was detected while spheres were observed in the pitch after cooling, confirming mesophase formation upon cooling after soaking. It was also found that the formation of spheres upon cooling accompanies the complete conversion of G2 into G1 and that the G1 formed hardly fuses while reheated to 723 K.

UR - http://www.scopus.com/inward/record.url?scp=0033878612&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0033878612&partnerID=8YFLogxK

U2 - 10.1016/S0008-6223(99)00152-9

DO - 10.1016/S0008-6223(99)00152-9

M3 - Article

VL - 38

SP - 749

EP - 758

JO - Carbon

JF - Carbon

SN - 0008-6223

IS - 5

ER -