Fractal analysis of solidification microstructure of high carbon high alloy cast roll manufactured by centrifugal casting

Masahiro Yamamoto, Ichihito Narita, Hirofumi Miyahara

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

The fractal dimension analysis was applied to the evaluation of primary dendrite and several eutectic structure morphologies in the high speed steel type cast iron for rolls which have been produced by the centrifugal cast technique. Initially, the affine parameter of the dendrite morphology of transparent organic alloy was evaluated based on the self-affine fractal theory. Primary γ dendrite and several eutectic structures crystallize in the high carbon high alloying element roll specimen. The microstructural morphology of sliced γ dendrite was analyzed by the self-similar fractal technique. The fractal dimension of each part of two-dimensionally-sliced dendrite varies from 1.05 to 1.13, and that of aggregation of dendrite's parts increases to 1.30. The fractal dimension of the primary dendrite among eutectic phases varies depending on the analysis area, and decreases with in decreasing of volume fraction of primary dendrite. In the specimen contained relatively high alloying elements, the round shape of sliced dendrite and the reduction of area fraction of primary dendrite cause to the difficulty of analyses using secondary dendrite arm spacing and fractal dimension of primary dendrite. Therefore, the fractal dimension of primary γ and γ+MC eutectic structure were evaluated. The fractal dimension analysis reveals that the morphology of dendrite and eutectic structure in segregated region slightly increases in comparison with the normal microstructure, and decreasing with the cooling velocity. Lower equilibrium partition coefficient of alloying elements and centrifugal force could cause the micro segregation of outer dendrites in roll specimen and complicated primary dendrite and γ+MC eutectic structure.

Original languageEnglish
Pages (from-to)2-9
Number of pages8
JournalTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
Volume99
Issue number2
DOIs
Publication statusPublished - Apr 8 2013

Fingerprint

centrifugal casting
Centrifugal casting
Dendrites (metallography)
cast alloys
Fractal dimension
dendrites
Fractals
Eutectics
solidification
Solidification
fractals
Carbon
microstructure
Microstructure
carbon
Alloying elements
eutectics
Steel
alloying
Cast iron

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

Cite this

@article{979b6de0dc1b44f5a98ecb496ecdc3b4,
title = "Fractal analysis of solidification microstructure of high carbon high alloy cast roll manufactured by centrifugal casting",
abstract = "The fractal dimension analysis was applied to the evaluation of primary dendrite and several eutectic structure morphologies in the high speed steel type cast iron for rolls which have been produced by the centrifugal cast technique. Initially, the affine parameter of the dendrite morphology of transparent organic alloy was evaluated based on the self-affine fractal theory. Primary γ dendrite and several eutectic structures crystallize in the high carbon high alloying element roll specimen. The microstructural morphology of sliced γ dendrite was analyzed by the self-similar fractal technique. The fractal dimension of each part of two-dimensionally-sliced dendrite varies from 1.05 to 1.13, and that of aggregation of dendrite's parts increases to 1.30. The fractal dimension of the primary dendrite among eutectic phases varies depending on the analysis area, and decreases with in decreasing of volume fraction of primary dendrite. In the specimen contained relatively high alloying elements, the round shape of sliced dendrite and the reduction of area fraction of primary dendrite cause to the difficulty of analyses using secondary dendrite arm spacing and fractal dimension of primary dendrite. Therefore, the fractal dimension of primary γ and γ+MC eutectic structure were evaluated. The fractal dimension analysis reveals that the morphology of dendrite and eutectic structure in segregated region slightly increases in comparison with the normal microstructure, and decreasing with the cooling velocity. Lower equilibrium partition coefficient of alloying elements and centrifugal force could cause the micro segregation of outer dendrites in roll specimen and complicated primary dendrite and γ+MC eutectic structure.",
author = "Masahiro Yamamoto and Ichihito Narita and Hirofumi Miyahara",
year = "2013",
month = "4",
day = "8",
doi = "10.2355/tetsutohagane.99.72",
language = "English",
volume = "99",
pages = "2--9",
journal = "Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan",
issn = "0021-1575",
publisher = "一般社団法人 日本鉄鋼協会",
number = "2",

}

TY - JOUR

T1 - Fractal analysis of solidification microstructure of high carbon high alloy cast roll manufactured by centrifugal casting

AU - Yamamoto, Masahiro

AU - Narita, Ichihito

AU - Miyahara, Hirofumi

PY - 2013/4/8

Y1 - 2013/4/8

N2 - The fractal dimension analysis was applied to the evaluation of primary dendrite and several eutectic structure morphologies in the high speed steel type cast iron for rolls which have been produced by the centrifugal cast technique. Initially, the affine parameter of the dendrite morphology of transparent organic alloy was evaluated based on the self-affine fractal theory. Primary γ dendrite and several eutectic structures crystallize in the high carbon high alloying element roll specimen. The microstructural morphology of sliced γ dendrite was analyzed by the self-similar fractal technique. The fractal dimension of each part of two-dimensionally-sliced dendrite varies from 1.05 to 1.13, and that of aggregation of dendrite's parts increases to 1.30. The fractal dimension of the primary dendrite among eutectic phases varies depending on the analysis area, and decreases with in decreasing of volume fraction of primary dendrite. In the specimen contained relatively high alloying elements, the round shape of sliced dendrite and the reduction of area fraction of primary dendrite cause to the difficulty of analyses using secondary dendrite arm spacing and fractal dimension of primary dendrite. Therefore, the fractal dimension of primary γ and γ+MC eutectic structure were evaluated. The fractal dimension analysis reveals that the morphology of dendrite and eutectic structure in segregated region slightly increases in comparison with the normal microstructure, and decreasing with the cooling velocity. Lower equilibrium partition coefficient of alloying elements and centrifugal force could cause the micro segregation of outer dendrites in roll specimen and complicated primary dendrite and γ+MC eutectic structure.

AB - The fractal dimension analysis was applied to the evaluation of primary dendrite and several eutectic structure morphologies in the high speed steel type cast iron for rolls which have been produced by the centrifugal cast technique. Initially, the affine parameter of the dendrite morphology of transparent organic alloy was evaluated based on the self-affine fractal theory. Primary γ dendrite and several eutectic structures crystallize in the high carbon high alloying element roll specimen. The microstructural morphology of sliced γ dendrite was analyzed by the self-similar fractal technique. The fractal dimension of each part of two-dimensionally-sliced dendrite varies from 1.05 to 1.13, and that of aggregation of dendrite's parts increases to 1.30. The fractal dimension of the primary dendrite among eutectic phases varies depending on the analysis area, and decreases with in decreasing of volume fraction of primary dendrite. In the specimen contained relatively high alloying elements, the round shape of sliced dendrite and the reduction of area fraction of primary dendrite cause to the difficulty of analyses using secondary dendrite arm spacing and fractal dimension of primary dendrite. Therefore, the fractal dimension of primary γ and γ+MC eutectic structure were evaluated. The fractal dimension analysis reveals that the morphology of dendrite and eutectic structure in segregated region slightly increases in comparison with the normal microstructure, and decreasing with the cooling velocity. Lower equilibrium partition coefficient of alloying elements and centrifugal force could cause the micro segregation of outer dendrites in roll specimen and complicated primary dendrite and γ+MC eutectic structure.

UR - http://www.scopus.com/inward/record.url?scp=84875718301&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84875718301&partnerID=8YFLogxK

U2 - 10.2355/tetsutohagane.99.72

DO - 10.2355/tetsutohagane.99.72

M3 - Article

AN - SCOPUS:84875718301

VL - 99

SP - 2

EP - 9

JO - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

JF - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

SN - 0021-1575

IS - 2

ER -