Heterogeneous structure and in vitro degradation behavior of wet-chemically derived nanocrystalline silicon-containing hydroxyapatite particles

Satoshi Hayakawa, Tomoko Kanaya, Kanji Tsuru, Yuki Shirosaki, Akiyoshi Osaka, Eiji Fujii, Koji Kawabata, Georgiana Gasqueres, Christian Bonhomme, Florence Babonneau, Christian Jäger, Hans Joachim Kleebe

Research output: Contribution to journalArticle

38 Citations (Scopus)


Nanocrystalline hydroxyapatite (HAp) and silicon-containing hydroxyapatite (SiHAp) particles were synthesized by a wet-chemical procedure and their heterogeneous structures involving a disordered phase were analyzed in detail by X-ray diffractometry (XRD), transmission electron microscopy (TEM), Fourier transform infrared (FTIR) spectroscopy and solid-state magic-angle spinning (MAS) nuclear magnetic resonance (NMR) spectroscopy. The effects of heterogeneous structure on in vitro biodegradability and the biologically active Ca(II)- and Si(IV)-releasing property of SiHAp particles were discussed. The 29Si NMR analysis revealed that the Si(IV) was incorporated in the HAp lattice in the form of Q0 (SiO44-orHSiO43-) species, accompanied by the formation of condensed silicate units outside the HAp lattice structure, where the fraction and amount of Q0 species in the HAp lattice depends on the Si content. The 31P and 1H NMR results agreed well with the XRD, TEM and FTIR results. NMR quantitative analysis results were explained by using a core-shell model assuming a simplified hexagonal shape of HAp covered with a disordered layer, where Si(IV) in Q 0 was incorporated in the HAp lattice and a disordered phase consisted of hydrated calcium phosphates involving polymeric silicate species and carbonate anions. With the increase in the Si content in the HAp lattice, the in vitro degradation rate of the SiHAps increased, while their crystallite size stayed nearly unchanged. The biologically active Ca(II)- and Si(IV)-releasing ability of the SiHAps was remarkably enhanced at the initial stage of reactions by an increase in the amount of Si(IV) incorporated in the HAp lattice but also by an increase of the amount of polymeric silicate species incorporated in the disordered phase.

Original languageEnglish
Pages (from-to)4856-4867
Number of pages12
JournalActa Biomaterialia
Issue number1
Publication statusPublished - Jan 1 2013


All Science Journal Classification (ASJC) codes

  • Biotechnology
  • Biomaterials
  • Biochemistry
  • Biomedical Engineering
  • Molecular Biology

Cite this