High heat load properties of TiC dispersed Mo alloys

K. Tokunaga, Y. Miura, N. Yoshida, T. Muroga, H. Kurishita, Y. Kitsunai, H. Kayano

Research output: Contribution to journalArticle

Abstract

A high heat load experiment of TiC dispersed Mo alloys using electron beams was carried out to investigate fundamental properties of thermal process due to high heat load as high heat flux materials such as the divertor tiles. As a result, although characteristic damage and gas emission of the TiC dispersed Mo alloys around the melting point are inferior to the PM-Mo, but those of the Mo-0.5wt%TiC and Mo-1.0wt%TiC below a temperature of about 2000°C were superior to polycrystalline Mo. Thus, their materials are expected to be suitable as high heat flux materials used below the recrystallization temperature. Results also indicate that it is necessary to release internal strain energy induced by the manufacturing process in order to decrease damage by grain growth and crack formation at high temperature, which was caused by migration of grain boundary and stress, respectively. Characterization of microstructure produced by the rolling process during manufacture is required to design improvement of the thermal conductivity.

Original languageEnglish
Pages (from-to)1197-1202
Number of pages6
JournalJournal of Nuclear Materials
Volume241-243
DOIs
Publication statusPublished - Feb 11 1997

All Science Journal Classification (ASJC) codes

  • Nuclear and High Energy Physics
  • Materials Science(all)
  • Nuclear Energy and Engineering

Fingerprint Dive into the research topics of 'High heat load properties of TiC dispersed Mo alloys'. Together they form a unique fingerprint.

Cite this