High strain rate superplasticity of the SiCp/7075 aluminum alloy composite made by a vortex method

Takeo Hikosaka, Tsunemichi Imai, Toshiro Kobayashi, Hiroyuki Toda

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

A SiCp/7075 aluminum alloy composite has been fabricated by a vortex method followed by squeeze casting, extrusion and rolling. The composites were hot rolled to the total rolling reduction of about 94% at temperatures between 573 K to 773 K and at a rolling strain per pass of 0.10. Superplastic characteristics such as microstructure and apparent activation energy were compared with these of the composites made by other processes in order to clarify the superplastic deformation mechanism. Fine grain size of about 1 μm was attained in the composite rolled at a temperature of 573 K and at the strain per pass of 0.1. In the case of rolling at 573 K, the composite obtained exhibited high strain rate superplasticity with a maximum elongation of about 230% at strain rate of 7 × 10-1 s-1 and at 798 K. Plots between ε̇1/n and σ showed linear relation when exponent of n=2 was assumed. Threshold stress obtained from the linear relations were largely dependent on the testing temperature. Apparent activation energy determined from relationship between strain rate and testing temperatures was 244 kJ/mol, which was smaller than that for the powder metallurgical and mechanically alloyed aluminum composites. It seems that there is no substantial difference of high strain rate superplastic mechanism between the composite fabricated by a vortex method and powder metallurgical aluminum alloy composites.

Original languageEnglish
Pages (from-to)169-174
Number of pages6
JournalKeikinzoku/Journal of Japan Institute of Light Metals
Volume51
Issue number3
DOIs
Publication statusPublished - Jan 1 2001
Externally publishedYes

Fingerprint

Superplasticity
Strain rate
Aluminum alloys
Vortex flow
Composite materials
Powders
Activation energy
Squeeze casting
Superplastic deformation
Temperature
Testing
Aluminum
Extrusion
Elongation
Microstructure

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Cite this

High strain rate superplasticity of the SiCp/7075 aluminum alloy composite made by a vortex method. / Hikosaka, Takeo; Imai, Tsunemichi; Kobayashi, Toshiro; Toda, Hiroyuki.

In: Keikinzoku/Journal of Japan Institute of Light Metals, Vol. 51, No. 3, 01.01.2001, p. 169-174.

Research output: Contribution to journalArticle

@article{938bccadb196461abaac029dd31e5a48,
title = "High strain rate superplasticity of the SiCp/7075 aluminum alloy composite made by a vortex method",
abstract = "A SiCp/7075 aluminum alloy composite has been fabricated by a vortex method followed by squeeze casting, extrusion and rolling. The composites were hot rolled to the total rolling reduction of about 94{\%} at temperatures between 573 K to 773 K and at a rolling strain per pass of 0.10. Superplastic characteristics such as microstructure and apparent activation energy were compared with these of the composites made by other processes in order to clarify the superplastic deformation mechanism. Fine grain size of about 1 μm was attained in the composite rolled at a temperature of 573 K and at the strain per pass of 0.1. In the case of rolling at 573 K, the composite obtained exhibited high strain rate superplasticity with a maximum elongation of about 230{\%} at strain rate of 7 × 10-1 s-1 and at 798 K. Plots between ε̇1/n and σ showed linear relation when exponent of n=2 was assumed. Threshold stress obtained from the linear relations were largely dependent on the testing temperature. Apparent activation energy determined from relationship between strain rate and testing temperatures was 244 kJ/mol, which was smaller than that for the powder metallurgical and mechanically alloyed aluminum composites. It seems that there is no substantial difference of high strain rate superplastic mechanism between the composite fabricated by a vortex method and powder metallurgical aluminum alloy composites.",
author = "Takeo Hikosaka and Tsunemichi Imai and Toshiro Kobayashi and Hiroyuki Toda",
year = "2001",
month = "1",
day = "1",
doi = "10.2464/jilm.51.169",
language = "English",
volume = "51",
pages = "169--174",
journal = "Keikinzoku/Journal of Japan Institute of Light Metals",
issn = "0451-5994",
publisher = "Keikinzoku Gakkai/Japan Institute of Light Metals",
number = "3",

}

TY - JOUR

T1 - High strain rate superplasticity of the SiCp/7075 aluminum alloy composite made by a vortex method

AU - Hikosaka, Takeo

AU - Imai, Tsunemichi

AU - Kobayashi, Toshiro

AU - Toda, Hiroyuki

PY - 2001/1/1

Y1 - 2001/1/1

N2 - A SiCp/7075 aluminum alloy composite has been fabricated by a vortex method followed by squeeze casting, extrusion and rolling. The composites were hot rolled to the total rolling reduction of about 94% at temperatures between 573 K to 773 K and at a rolling strain per pass of 0.10. Superplastic characteristics such as microstructure and apparent activation energy were compared with these of the composites made by other processes in order to clarify the superplastic deformation mechanism. Fine grain size of about 1 μm was attained in the composite rolled at a temperature of 573 K and at the strain per pass of 0.1. In the case of rolling at 573 K, the composite obtained exhibited high strain rate superplasticity with a maximum elongation of about 230% at strain rate of 7 × 10-1 s-1 and at 798 K. Plots between ε̇1/n and σ showed linear relation when exponent of n=2 was assumed. Threshold stress obtained from the linear relations were largely dependent on the testing temperature. Apparent activation energy determined from relationship between strain rate and testing temperatures was 244 kJ/mol, which was smaller than that for the powder metallurgical and mechanically alloyed aluminum composites. It seems that there is no substantial difference of high strain rate superplastic mechanism between the composite fabricated by a vortex method and powder metallurgical aluminum alloy composites.

AB - A SiCp/7075 aluminum alloy composite has been fabricated by a vortex method followed by squeeze casting, extrusion and rolling. The composites were hot rolled to the total rolling reduction of about 94% at temperatures between 573 K to 773 K and at a rolling strain per pass of 0.10. Superplastic characteristics such as microstructure and apparent activation energy were compared with these of the composites made by other processes in order to clarify the superplastic deformation mechanism. Fine grain size of about 1 μm was attained in the composite rolled at a temperature of 573 K and at the strain per pass of 0.1. In the case of rolling at 573 K, the composite obtained exhibited high strain rate superplasticity with a maximum elongation of about 230% at strain rate of 7 × 10-1 s-1 and at 798 K. Plots between ε̇1/n and σ showed linear relation when exponent of n=2 was assumed. Threshold stress obtained from the linear relations were largely dependent on the testing temperature. Apparent activation energy determined from relationship between strain rate and testing temperatures was 244 kJ/mol, which was smaller than that for the powder metallurgical and mechanically alloyed aluminum composites. It seems that there is no substantial difference of high strain rate superplastic mechanism between the composite fabricated by a vortex method and powder metallurgical aluminum alloy composites.

UR - http://www.scopus.com/inward/record.url?scp=0035269931&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0035269931&partnerID=8YFLogxK

U2 - 10.2464/jilm.51.169

DO - 10.2464/jilm.51.169

M3 - Article

VL - 51

SP - 169

EP - 174

JO - Keikinzoku/Journal of Japan Institute of Light Metals

JF - Keikinzoku/Journal of Japan Institute of Light Metals

SN - 0451-5994

IS - 3

ER -