High temperature deformation behaviour of ultra-high purity polycrystalline silicon

Yuichi Hirakawa, Koichi Kawahara, Fuyuki Yoshida, Hideharu Nakashima, Hiroshi Abe

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

Ultra-high purity polycrystalline silicon was deformed by compression at temperatures from 1123 to 1643 K and at strain rates from 1×10-5 to 1×10-4 s-1, and the dislocation structures developed during high temperature deformation were also observed by transmission electron microscopy to obtain the fundamental knowledge on the high temperature deformation of polycrystalline silicon. It was found that the flow stress for the polycrystalline silicon deformed at 1123 K and at a strain rate of 1×10-4 s-1 was much greater than that for the single crystalline silicon (FZ-Si) deformed under the same condition. The observed difference in the flow stress was considered to be attributed to the existence of stable and fine twin boundaries, which could operate as the barriers for dislocation motion. The steady-state deformation, where the flow stress was almost independent of strain, was observed at temperatures over 1473 K. The stress exponents, n, were found to be about 7 at 1473 K and about 5 at 1573 and 1643 K, respectively. The activation energy for deformation at temperatures, where the stress exponent was about 5, was in good agreement with that for the lattice self-diffusion in silicon. Therefore, it is concluded that the recovery controlling mechanism governed by the lattice diffusion is the rate controlling mechanism for the deformation of polycrystalline silicon at these temperatures.

Original languageEnglish
Pages (from-to)1093-1096
Number of pages4
JournalNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
Volume63
Issue number9
DOIs
Publication statusPublished - Jan 1 1999

Fingerprint

Polysilicon
purity
silicon
Plastic flow
Silicon
Temperature
strain rate
Strain rate
exponents
temperature
Activation energy
recovery
activation energy
Crystalline materials
Transmission electron microscopy
Recovery
transmission electron microscopy

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

Cite this

High temperature deformation behaviour of ultra-high purity polycrystalline silicon. / Hirakawa, Yuichi; Kawahara, Koichi; Yoshida, Fuyuki; Nakashima, Hideharu; Abe, Hiroshi.

In: Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals, Vol. 63, No. 9, 01.01.1999, p. 1093-1096.

Research output: Contribution to journalArticle

Hirakawa, Yuichi ; Kawahara, Koichi ; Yoshida, Fuyuki ; Nakashima, Hideharu ; Abe, Hiroshi. / High temperature deformation behaviour of ultra-high purity polycrystalline silicon. In: Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals. 1999 ; Vol. 63, No. 9. pp. 1093-1096.
@article{5bd776914900420f9fe710b1886c4391,
title = "High temperature deformation behaviour of ultra-high purity polycrystalline silicon",
abstract = "Ultra-high purity polycrystalline silicon was deformed by compression at temperatures from 1123 to 1643 K and at strain rates from 1×10-5 to 1×10-4 s-1, and the dislocation structures developed during high temperature deformation were also observed by transmission electron microscopy to obtain the fundamental knowledge on the high temperature deformation of polycrystalline silicon. It was found that the flow stress for the polycrystalline silicon deformed at 1123 K and at a strain rate of 1×10-4 s-1 was much greater than that for the single crystalline silicon (FZ-Si) deformed under the same condition. The observed difference in the flow stress was considered to be attributed to the existence of stable and fine twin boundaries, which could operate as the barriers for dislocation motion. The steady-state deformation, where the flow stress was almost independent of strain, was observed at temperatures over 1473 K. The stress exponents, n, were found to be about 7 at 1473 K and about 5 at 1573 and 1643 K, respectively. The activation energy for deformation at temperatures, where the stress exponent was about 5, was in good agreement with that for the lattice self-diffusion in silicon. Therefore, it is concluded that the recovery controlling mechanism governed by the lattice diffusion is the rate controlling mechanism for the deformation of polycrystalline silicon at these temperatures.",
author = "Yuichi Hirakawa and Koichi Kawahara and Fuyuki Yoshida and Hideharu Nakashima and Hiroshi Abe",
year = "1999",
month = "1",
day = "1",
doi = "10.2320/jinstmet1952.63.9_1093",
language = "English",
volume = "63",
pages = "1093--1096",
journal = "Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals",
issn = "0021-4876",
publisher = "公益社団法人 日本金属学会",
number = "9",

}

TY - JOUR

T1 - High temperature deformation behaviour of ultra-high purity polycrystalline silicon

AU - Hirakawa, Yuichi

AU - Kawahara, Koichi

AU - Yoshida, Fuyuki

AU - Nakashima, Hideharu

AU - Abe, Hiroshi

PY - 1999/1/1

Y1 - 1999/1/1

N2 - Ultra-high purity polycrystalline silicon was deformed by compression at temperatures from 1123 to 1643 K and at strain rates from 1×10-5 to 1×10-4 s-1, and the dislocation structures developed during high temperature deformation were also observed by transmission electron microscopy to obtain the fundamental knowledge on the high temperature deformation of polycrystalline silicon. It was found that the flow stress for the polycrystalline silicon deformed at 1123 K and at a strain rate of 1×10-4 s-1 was much greater than that for the single crystalline silicon (FZ-Si) deformed under the same condition. The observed difference in the flow stress was considered to be attributed to the existence of stable and fine twin boundaries, which could operate as the barriers for dislocation motion. The steady-state deformation, where the flow stress was almost independent of strain, was observed at temperatures over 1473 K. The stress exponents, n, were found to be about 7 at 1473 K and about 5 at 1573 and 1643 K, respectively. The activation energy for deformation at temperatures, where the stress exponent was about 5, was in good agreement with that for the lattice self-diffusion in silicon. Therefore, it is concluded that the recovery controlling mechanism governed by the lattice diffusion is the rate controlling mechanism for the deformation of polycrystalline silicon at these temperatures.

AB - Ultra-high purity polycrystalline silicon was deformed by compression at temperatures from 1123 to 1643 K and at strain rates from 1×10-5 to 1×10-4 s-1, and the dislocation structures developed during high temperature deformation were also observed by transmission electron microscopy to obtain the fundamental knowledge on the high temperature deformation of polycrystalline silicon. It was found that the flow stress for the polycrystalline silicon deformed at 1123 K and at a strain rate of 1×10-4 s-1 was much greater than that for the single crystalline silicon (FZ-Si) deformed under the same condition. The observed difference in the flow stress was considered to be attributed to the existence of stable and fine twin boundaries, which could operate as the barriers for dislocation motion. The steady-state deformation, where the flow stress was almost independent of strain, was observed at temperatures over 1473 K. The stress exponents, n, were found to be about 7 at 1473 K and about 5 at 1573 and 1643 K, respectively. The activation energy for deformation at temperatures, where the stress exponent was about 5, was in good agreement with that for the lattice self-diffusion in silicon. Therefore, it is concluded that the recovery controlling mechanism governed by the lattice diffusion is the rate controlling mechanism for the deformation of polycrystalline silicon at these temperatures.

UR - http://www.scopus.com/inward/record.url?scp=0033318186&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0033318186&partnerID=8YFLogxK

U2 - 10.2320/jinstmet1952.63.9_1093

DO - 10.2320/jinstmet1952.63.9_1093

M3 - Article

AN - SCOPUS:0033318186

VL - 63

SP - 1093

EP - 1096

JO - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals

JF - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals

SN - 0021-4876

IS - 9

ER -