Impact of severe plastic deformation on microstructure and hydrogen storage of titanium-iron-manganese intermetallics

Kaveh Edalati, Motoaki Matsuo, Hoda Emami, Shota Itano, Ali Alhamidi, Aleksandar Staykov, David J. Smith, Shin ichi Orimo, Etsuo Akiba, Zenji Horita

Research output: Contribution to journalArticle

16 Citations (Scopus)

Abstract

TiFe1-xMnx intermetallics (x = 0, 0.15 and 0.3) were severely deformed by high-pressure torsion (HPT) to enhance their activation and air resistivity for hydrogenation. While the as-cast ingots hardly absorbed hydrogen (TiFe0.7Mn0.3 exhibited slow activation after an incubation period), the HPT-processed samples absorbed hydrogen quickly at room temperature even after air exposure. The improvement of hydrogen storage performance was due to the formation of lattice defects and amorphous regions, which act as channels for hydrogen diffusion. Rietveld analyses and first-principles calculations showed that Mn addition expands the lattice and reduces the hydride formation energy, and thus decreases the hydrogenation/activation pressure.

Original languageEnglish
Pages (from-to)108-111
Number of pages4
JournalScripta Materialia
Volume124
DOIs
Publication statusPublished - Nov 1 2016

Fingerprint

Hydrogen storage
Manganese
Titanium
plastic deformation
Intermetallics
intermetallics
manganese
Hydrogen
Plastic deformation
Iron
titanium
Chemical activation
iron
Torsional stress
microstructure
Microstructure
Hydrogenation
activation
hydrogen
hydrogenation

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys

Cite this

Impact of severe plastic deformation on microstructure and hydrogen storage of titanium-iron-manganese intermetallics. / Edalati, Kaveh; Matsuo, Motoaki; Emami, Hoda; Itano, Shota; Alhamidi, Ali; Staykov, Aleksandar; Smith, David J.; Orimo, Shin ichi; Akiba, Etsuo; Horita, Zenji.

In: Scripta Materialia, Vol. 124, 01.11.2016, p. 108-111.

Research output: Contribution to journalArticle

Edalati, Kaveh ; Matsuo, Motoaki ; Emami, Hoda ; Itano, Shota ; Alhamidi, Ali ; Staykov, Aleksandar ; Smith, David J. ; Orimo, Shin ichi ; Akiba, Etsuo ; Horita, Zenji. / Impact of severe plastic deformation on microstructure and hydrogen storage of titanium-iron-manganese intermetallics. In: Scripta Materialia. 2016 ; Vol. 124. pp. 108-111.
@article{d71fc7d7093c4360a672bf962de1b22b,
title = "Impact of severe plastic deformation on microstructure and hydrogen storage of titanium-iron-manganese intermetallics",
abstract = "TiFe1-xMnx intermetallics (x = 0, 0.15 and 0.3) were severely deformed by high-pressure torsion (HPT) to enhance their activation and air resistivity for hydrogenation. While the as-cast ingots hardly absorbed hydrogen (TiFe0.7Mn0.3 exhibited slow activation after an incubation period), the HPT-processed samples absorbed hydrogen quickly at room temperature even after air exposure. The improvement of hydrogen storage performance was due to the formation of lattice defects and amorphous regions, which act as channels for hydrogen diffusion. Rietveld analyses and first-principles calculations showed that Mn addition expands the lattice and reduces the hydride formation energy, and thus decreases the hydrogenation/activation pressure.",
author = "Kaveh Edalati and Motoaki Matsuo and Hoda Emami and Shota Itano and Ali Alhamidi and Aleksandar Staykov and Smith, {David J.} and Orimo, {Shin ichi} and Etsuo Akiba and Zenji Horita",
year = "2016",
month = "11",
day = "1",
doi = "10.1016/j.scriptamat.2016.07.007",
language = "English",
volume = "124",
pages = "108--111",
journal = "Scripta Materialia",
issn = "1359-6462",
publisher = "Elsevier Limited",

}

TY - JOUR

T1 - Impact of severe plastic deformation on microstructure and hydrogen storage of titanium-iron-manganese intermetallics

AU - Edalati, Kaveh

AU - Matsuo, Motoaki

AU - Emami, Hoda

AU - Itano, Shota

AU - Alhamidi, Ali

AU - Staykov, Aleksandar

AU - Smith, David J.

AU - Orimo, Shin ichi

AU - Akiba, Etsuo

AU - Horita, Zenji

PY - 2016/11/1

Y1 - 2016/11/1

N2 - TiFe1-xMnx intermetallics (x = 0, 0.15 and 0.3) were severely deformed by high-pressure torsion (HPT) to enhance their activation and air resistivity for hydrogenation. While the as-cast ingots hardly absorbed hydrogen (TiFe0.7Mn0.3 exhibited slow activation after an incubation period), the HPT-processed samples absorbed hydrogen quickly at room temperature even after air exposure. The improvement of hydrogen storage performance was due to the formation of lattice defects and amorphous regions, which act as channels for hydrogen diffusion. Rietveld analyses and first-principles calculations showed that Mn addition expands the lattice and reduces the hydride formation energy, and thus decreases the hydrogenation/activation pressure.

AB - TiFe1-xMnx intermetallics (x = 0, 0.15 and 0.3) were severely deformed by high-pressure torsion (HPT) to enhance their activation and air resistivity for hydrogenation. While the as-cast ingots hardly absorbed hydrogen (TiFe0.7Mn0.3 exhibited slow activation after an incubation period), the HPT-processed samples absorbed hydrogen quickly at room temperature even after air exposure. The improvement of hydrogen storage performance was due to the formation of lattice defects and amorphous regions, which act as channels for hydrogen diffusion. Rietveld analyses and first-principles calculations showed that Mn addition expands the lattice and reduces the hydride formation energy, and thus decreases the hydrogenation/activation pressure.

UR - http://www.scopus.com/inward/record.url?scp=84978204265&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84978204265&partnerID=8YFLogxK

U2 - 10.1016/j.scriptamat.2016.07.007

DO - 10.1016/j.scriptamat.2016.07.007

M3 - Article

AN - SCOPUS:84978204265

VL - 124

SP - 108

EP - 111

JO - Scripta Materialia

JF - Scripta Materialia

SN - 1359-6462

ER -