Improvement in electrochromic stability of electrodeposited nickel hydroxide thin film

C. Natarajan, H. Matsumoto, G. Nogami

Research output: Contribution to journalArticlepeer-review

126 Citations (Scopus)

Abstract

The electrochromic nickel hydroxide thin film was anodically deposited from an aqueous solution. The effect of solution temperature, postheat-treatment temperature, and addition of cadmium on the electrochromic behavior (color/bleach durability cycle, response time, and coloration efficiency of the nickel hydroxide films in NaOH) were investigated. A significant increase in the color/bleach durability cycle from 500 (for the as-deposited film) to more than 5000 cycles (for the heat-treated film) was observed. The addition of cadmium increased the utilization of the active materials. It was found that the coloration efficiency was 40 cm2/C and coloration and bleaching response time were 20 to 30 s and 8 to 10 s, respectively. The change in the electrochromic properties with heat-treatment temperature is discussed based on the physical and electrochemical analysis.

Original languageEnglish
Pages (from-to)121-126
Number of pages6
JournalJournal of the Electrochemical Society
Volume144
Issue number1
DOIs
Publication statusPublished - Jan 1997
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Renewable Energy, Sustainability and the Environment
  • Surfaces, Coatings and Films
  • Electrochemistry
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Improvement in electrochromic stability of electrodeposited nickel hydroxide thin film'. Together they form a unique fingerprint.

Cite this