Influence of aging condition and reversion austenite on fatigue property of the 300 grade 18Ni maraging steel

Michihiko Moriyama, Setsuo Takaki, Norio Kawagoishi

Research output: Contribution to journalArticle

10 Citations (Scopus)

Abstract

The influence of aging condition on fatigue strength of the 300 grade 18Ni maraging steel has been investigated in relation to the behavior of age hardening and the formation of reversion austenite. In this study, rotating bending fatigue tests were performed for three series of specimens with different aging condition; as solution-treated without aging, aged for various time at 753 K which is the temperature applied for the industrial aging treatment, and over-aged to form a small amount of reversion austenite. Effect of reversion austenite on fatigue strength was examined using specimens with the same static strength which had been controlled by varying aging temperature and time, namely under-aging or over-aging. The main results obtained are as follows. (1) In the case of 753 K aging, the fatigue limits of specimens aged for 11 ks to 48 ks were nearly the same value, although an under-aged (2.8 ks) specimen has as much lower value as a solution-treated specimen without aging treatment. (2) A small amount of reversion austenite is effective for increasing fatigue resistance. For instance, 2 vol % of austenite was enough for improving fatigue limit of the maraging steel used, from 580 MPa to 640 MPa at the same hardness level of Hv 610.

Original languageEnglish
Pages (from-to)631-637
Number of pages7
JournalZairyo/Journal of the Society of Materials Science, Japan
Volume49
Issue number6
DOIs
Publication statusPublished - Jun 2000

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Influence of aging condition and reversion austenite on fatigue property of the 300 grade 18Ni maraging steel'. Together they form a unique fingerprint.

Cite this