Influence of crystal orientation on the processing of copper single crystals by ECAP

Yukihide Fukuda, Keiichiro Oh-Ishi, Minoru Furukawa, Zenji Horita, Terence G. Langdon

    Research output: Contribution to journalArticlepeer-review

    31 Citations (Scopus)

    Abstract

    Single crystals of high-purity copper, having two different orientations, were pressed through one pass in equal-channel angular pressing (ECAP) at room temperature and then examined using several different analytical techniques. For both orientations, it is shown that elongated arrays of cells or subgrains are formed in the first pass with their long axes aligned parallel to the primary (1̄1̄1̄)[1̄10]} slip system. The average width of these subgrains was measured as ∼0.2 μm which is similar to the equilibrium grain size reported in polycrystalline Cu after processing by ECAP. These results confirm earlier observations using an aluminum single crystal except only that the subgrain width in copper is significantly smaller. This difference is attributed to the lower stacking-fault energy in copper and the consequent low rate of recovery.

    Original languageEnglish
    Pages (from-to)1501-1511
    Number of pages11
    JournalJournal of Materials Science
    Volume42
    Issue number5
    DOIs
    Publication statusPublished - Mar 2007

    All Science Journal Classification (ASJC) codes

    • Materials Science(all)
    • Mechanics of Materials
    • Mechanical Engineering

    Fingerprint

    Dive into the research topics of 'Influence of crystal orientation on the processing of copper single crystals by ECAP'. Together they form a unique fingerprint.

    Cite this