Influence of strain rate on grain size dependence of strength of sheet steel

Kazuya Miura, Shusaku Takagi, Osamu Furukimi, Shinji Tanimura

    Research output: Contribution to journalArticlepeer-review

    14 Citations (Scopus)

    Abstract

    Influence of strain rates on the grain size dependence of tensile deformation behavior was investigated on a mild steel and solid-solute hardened 440MPa and 590MPa grade steels. The grain size of these steels was ranged from 0.005mm to 0.2mm in diameter. Tensile tests were performed at strain rates of 0.02/s and 2/s with an Instron tensile machine, and at 2000/s with a split-Hopkinson pressure bar apparatus. The relationships between yield strength and grain size of the steels investigated were well represented by the Hall-Petch relationship, and the energy absorbed during deformation at the strain rate of 2000/s increased for finer grain size. The grain size dependence of the yield strength of the 440MPa and 590MPa grade steels was intensified with increase in strain rate, while, those of the mild steel were almost independent of the strain rate. The n-value of the mild steel was remarkably reduced with an increase of the strain rate. The grain size, however, didn't affect the n-value.

    Original languageEnglish
    Pages (from-to)1053-1058
    Number of pages6
    JournalZairyo/Journal of the Society of Materials Science, Japan
    Volume47
    Issue number10
    DOIs
    Publication statusPublished - Oct 1998

    All Science Journal Classification (ASJC) codes

    • Materials Science(all)
    • Condensed Matter Physics
    • Mechanics of Materials
    • Mechanical Engineering

    Fingerprint

    Dive into the research topics of 'Influence of strain rate on grain size dependence of strength of sheet steel'. Together they form a unique fingerprint.

    Cite this