Intergrated evaluation method for fatigue limit of notched steel with ΔKth value

T. Matsueda, Hiroshi Noguchi

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

It is the big problem to evaluate the fatigue limit σw in order to safely design structures and machines. Under the condition of the fatigue crack initiation limit σw1, the present author defined the initial crack size √area using the characteristic elastic field of the notch, the half length of the fatigue crack a and a notch depth t. Using this √area, the methods of calculating ΔKth and σw1 were proposed. In addition to it, in this condition it is made sure that ΔKth exists on the band from ΔK th prediction line of the micro fatigue crack within 18% error. Using ΔKth calculated by the prediction line and the value of Vi, this evaluating method of σw1 was confirmed with annealed 0.35% carbon steel. As a result, it was confirmed that this method to evaluate σw1 is within 18% error. Moreover it was also confirmed that the σw1 value by this prediction method is within 10% error when the predicted σw1 value is greater than σw2.

Original languageEnglish
Title of host publication19th European Conference on Fracture
Subtitle of host publicationFracture Mechanics for Durability, Reliability and Safety, ECF 2012
PublisherEuropean Conference on Fracture, ECF
ISBN (Print)978-5-905576-18-8
Publication statusPublished - Jan 1 2012
Event19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012 - Kazan, Russian Federation
Duration: Aug 26 2012Aug 31 2012

Publication series

Name19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012

Other

Other19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012
CountryRussian Federation
CityKazan
Period8/26/128/31/12

Fingerprint

Fatigue of materials
Steel
Crack initiation
Carbon steel
Cracks
Fatigue cracks

All Science Journal Classification (ASJC) codes

  • Safety, Risk, Reliability and Quality

Cite this

Matsueda, T., & Noguchi, H. (2012). Intergrated evaluation method for fatigue limit of notched steel with ΔKth value. In 19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012 (19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012). European Conference on Fracture, ECF.

Intergrated evaluation method for fatigue limit of notched steel with ΔKth value. / Matsueda, T.; Noguchi, Hiroshi.

19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012. European Conference on Fracture, ECF, 2012. (19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Matsueda, T & Noguchi, H 2012, Intergrated evaluation method for fatigue limit of notched steel with ΔKth value. in 19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012. 19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012, European Conference on Fracture, ECF, 19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012, Kazan, Russian Federation, 8/26/12.
Matsueda T, Noguchi H. Intergrated evaluation method for fatigue limit of notched steel with ΔKth value. In 19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012. European Conference on Fracture, ECF. 2012. (19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012).
Matsueda, T. ; Noguchi, Hiroshi. / Intergrated evaluation method for fatigue limit of notched steel with ΔKth value. 19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012. European Conference on Fracture, ECF, 2012. (19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012).
@inproceedings{6fcd3dceaaa14fa8adb352733b363e68,
title = "Intergrated evaluation method for fatigue limit of notched steel with ΔKth value",
abstract = "It is the big problem to evaluate the fatigue limit σw in order to safely design structures and machines. Under the condition of the fatigue crack initiation limit σw1, the present author defined the initial crack size √area using the characteristic elastic field of the notch, the half length of the fatigue crack a and a notch depth t. Using this √area, the methods of calculating ΔKth and σw1 were proposed. In addition to it, in this condition it is made sure that ΔKth exists on the band from ΔK th prediction line of the micro fatigue crack within 18{\%} error. Using ΔKth calculated by the prediction line and the value of Vi, this evaluating method of σw1 was confirmed with annealed 0.35{\%} carbon steel. As a result, it was confirmed that this method to evaluate σw1 is within 18{\%} error. Moreover it was also confirmed that the σw1 value by this prediction method is within 10{\%} error when the predicted σw1 value is greater than σw2.",
author = "T. Matsueda and Hiroshi Noguchi",
year = "2012",
month = "1",
day = "1",
language = "English",
isbn = "978-5-905576-18-8",
series = "19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012",
publisher = "European Conference on Fracture, ECF",
booktitle = "19th European Conference on Fracture",

}

TY - GEN

T1 - Intergrated evaluation method for fatigue limit of notched steel with ΔKth value

AU - Matsueda, T.

AU - Noguchi, Hiroshi

PY - 2012/1/1

Y1 - 2012/1/1

N2 - It is the big problem to evaluate the fatigue limit σw in order to safely design structures and machines. Under the condition of the fatigue crack initiation limit σw1, the present author defined the initial crack size √area using the characteristic elastic field of the notch, the half length of the fatigue crack a and a notch depth t. Using this √area, the methods of calculating ΔKth and σw1 were proposed. In addition to it, in this condition it is made sure that ΔKth exists on the band from ΔK th prediction line of the micro fatigue crack within 18% error. Using ΔKth calculated by the prediction line and the value of Vi, this evaluating method of σw1 was confirmed with annealed 0.35% carbon steel. As a result, it was confirmed that this method to evaluate σw1 is within 18% error. Moreover it was also confirmed that the σw1 value by this prediction method is within 10% error when the predicted σw1 value is greater than σw2.

AB - It is the big problem to evaluate the fatigue limit σw in order to safely design structures and machines. Under the condition of the fatigue crack initiation limit σw1, the present author defined the initial crack size √area using the characteristic elastic field of the notch, the half length of the fatigue crack a and a notch depth t. Using this √area, the methods of calculating ΔKth and σw1 were proposed. In addition to it, in this condition it is made sure that ΔKth exists on the band from ΔK th prediction line of the micro fatigue crack within 18% error. Using ΔKth calculated by the prediction line and the value of Vi, this evaluating method of σw1 was confirmed with annealed 0.35% carbon steel. As a result, it was confirmed that this method to evaluate σw1 is within 18% error. Moreover it was also confirmed that the σw1 value by this prediction method is within 10% error when the predicted σw1 value is greater than σw2.

UR - http://www.scopus.com/inward/record.url?scp=84905455387&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84905455387&partnerID=8YFLogxK

M3 - Conference contribution

AN - SCOPUS:84905455387

SN - 978-5-905576-18-8

T3 - 19th European Conference on Fracture: Fracture Mechanics for Durability, Reliability and Safety, ECF 2012

BT - 19th European Conference on Fracture

PB - European Conference on Fracture, ECF

ER -