Intrinsic factors that trigger the coaxing effect in binary Fe-C ferritic alloys with a focus on strain aging

Motomichi Koyama, Bohong Ren, Nobuyuki Yoshimura, Eisaku Sakurada, Kohsaku Ushioda, Hiroshi Noguchi

Research output: Contribution to journalArticle

Abstract

The coaxing effect has been recognized as a phenomenon that enhances the fatigue resistance associated with work hardening and strainage hardening. To uncover the intrinsic factors that affect the degree of coaxing effect, rotating bending fatigue tests including a process of stepwise stress increases every 107 cycles were carried out at ambient temperature in interstitial free steel and binary Fe-C ferritic alloys. The effects of the work hardening capacity, aging time, stress amplitude increment, and carbon concentration were examined in this simple alloy system. The work hardening capacity was changed by controlling carbon state in a Fe-0.017C (wt%) steel. However, the degree of coaxing effect did not show a significant correlation with work hardening capacity. For the effect of aging time, a fatigue test at a high stress amplitude was interrupted, aged for 2 weeks, and subsequently restarted. Although this process is sufficient to induce strain-age hardening in terms of aging time and plastic strain, a fatigue life of the aged steel was not comparable to that with the coaxing effect. Moreover, an increase in stress increment for each step deteriorated a degree of coaxing effect. It was concluded that the effect of work hardening is minor, and the other factors affecting strain-age hardening must be optimized simultaneously to show a coaxing effect. In addition, the degree of coaxing effect of smooth steel specimens was predominantly controlled by the intergranular fatigue crack initiation behavior. Consequently, a considerable amount of solute carbon and an alternate process for the stress amplitude increment and aging time are required for strain-age hardening that suppresses intergranular fatigue crack initiation.

Original languageEnglish
Pages (from-to)660-666
Number of pages7
JournalTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
Volume103
Issue number11
DOIs
Publication statusPublished - Jan 1 2017

Fingerprint

Intrinsic Factor
precipitation hardening
Strain hardening
Aging of materials
actuators
Steel
work hardening
Age hardening
Fatigue of materials
Carbon
steels
Crack initiation
fatigue tests
crack initiation
carbon
bending fatigue
Hardening
Plastic deformation
fatigue life
hardening

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

Cite this

Intrinsic factors that trigger the coaxing effect in binary Fe-C ferritic alloys with a focus on strain aging. / Koyama, Motomichi; Ren, Bohong; Yoshimura, Nobuyuki; Sakurada, Eisaku; Ushioda, Kohsaku; Noguchi, Hiroshi.

In: Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, Vol. 103, No. 11, 01.01.2017, p. 660-666.

Research output: Contribution to journalArticle

Koyama, Motomichi ; Ren, Bohong ; Yoshimura, Nobuyuki ; Sakurada, Eisaku ; Ushioda, Kohsaku ; Noguchi, Hiroshi. / Intrinsic factors that trigger the coaxing effect in binary Fe-C ferritic alloys with a focus on strain aging. In: Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan. 2017 ; Vol. 103, No. 11. pp. 660-666.
@article{720c111d27a04e7badd3e6e301d79a09,
title = "Intrinsic factors that trigger the coaxing effect in binary Fe-C ferritic alloys with a focus on strain aging",
abstract = "The coaxing effect has been recognized as a phenomenon that enhances the fatigue resistance associated with work hardening and strainage hardening. To uncover the intrinsic factors that affect the degree of coaxing effect, rotating bending fatigue tests including a process of stepwise stress increases every 107 cycles were carried out at ambient temperature in interstitial free steel and binary Fe-C ferritic alloys. The effects of the work hardening capacity, aging time, stress amplitude increment, and carbon concentration were examined in this simple alloy system. The work hardening capacity was changed by controlling carbon state in a Fe-0.017C (wt{\%}) steel. However, the degree of coaxing effect did not show a significant correlation with work hardening capacity. For the effect of aging time, a fatigue test at a high stress amplitude was interrupted, aged for 2 weeks, and subsequently restarted. Although this process is sufficient to induce strain-age hardening in terms of aging time and plastic strain, a fatigue life of the aged steel was not comparable to that with the coaxing effect. Moreover, an increase in stress increment for each step deteriorated a degree of coaxing effect. It was concluded that the effect of work hardening is minor, and the other factors affecting strain-age hardening must be optimized simultaneously to show a coaxing effect. In addition, the degree of coaxing effect of smooth steel specimens was predominantly controlled by the intergranular fatigue crack initiation behavior. Consequently, a considerable amount of solute carbon and an alternate process for the stress amplitude increment and aging time are required for strain-age hardening that suppresses intergranular fatigue crack initiation.",
author = "Motomichi Koyama and Bohong Ren and Nobuyuki Yoshimura and Eisaku Sakurada and Kohsaku Ushioda and Hiroshi Noguchi",
year = "2017",
month = "1",
day = "1",
doi = "10.2355/tetsutohagane.TETSU-2017-043",
language = "English",
volume = "103",
pages = "660--666",
journal = "Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan",
issn = "0021-1575",
publisher = "一般社団法人 日本鉄鋼協会",
number = "11",

}

TY - JOUR

T1 - Intrinsic factors that trigger the coaxing effect in binary Fe-C ferritic alloys with a focus on strain aging

AU - Koyama, Motomichi

AU - Ren, Bohong

AU - Yoshimura, Nobuyuki

AU - Sakurada, Eisaku

AU - Ushioda, Kohsaku

AU - Noguchi, Hiroshi

PY - 2017/1/1

Y1 - 2017/1/1

N2 - The coaxing effect has been recognized as a phenomenon that enhances the fatigue resistance associated with work hardening and strainage hardening. To uncover the intrinsic factors that affect the degree of coaxing effect, rotating bending fatigue tests including a process of stepwise stress increases every 107 cycles were carried out at ambient temperature in interstitial free steel and binary Fe-C ferritic alloys. The effects of the work hardening capacity, aging time, stress amplitude increment, and carbon concentration were examined in this simple alloy system. The work hardening capacity was changed by controlling carbon state in a Fe-0.017C (wt%) steel. However, the degree of coaxing effect did not show a significant correlation with work hardening capacity. For the effect of aging time, a fatigue test at a high stress amplitude was interrupted, aged for 2 weeks, and subsequently restarted. Although this process is sufficient to induce strain-age hardening in terms of aging time and plastic strain, a fatigue life of the aged steel was not comparable to that with the coaxing effect. Moreover, an increase in stress increment for each step deteriorated a degree of coaxing effect. It was concluded that the effect of work hardening is minor, and the other factors affecting strain-age hardening must be optimized simultaneously to show a coaxing effect. In addition, the degree of coaxing effect of smooth steel specimens was predominantly controlled by the intergranular fatigue crack initiation behavior. Consequently, a considerable amount of solute carbon and an alternate process for the stress amplitude increment and aging time are required for strain-age hardening that suppresses intergranular fatigue crack initiation.

AB - The coaxing effect has been recognized as a phenomenon that enhances the fatigue resistance associated with work hardening and strainage hardening. To uncover the intrinsic factors that affect the degree of coaxing effect, rotating bending fatigue tests including a process of stepwise stress increases every 107 cycles were carried out at ambient temperature in interstitial free steel and binary Fe-C ferritic alloys. The effects of the work hardening capacity, aging time, stress amplitude increment, and carbon concentration were examined in this simple alloy system. The work hardening capacity was changed by controlling carbon state in a Fe-0.017C (wt%) steel. However, the degree of coaxing effect did not show a significant correlation with work hardening capacity. For the effect of aging time, a fatigue test at a high stress amplitude was interrupted, aged for 2 weeks, and subsequently restarted. Although this process is sufficient to induce strain-age hardening in terms of aging time and plastic strain, a fatigue life of the aged steel was not comparable to that with the coaxing effect. Moreover, an increase in stress increment for each step deteriorated a degree of coaxing effect. It was concluded that the effect of work hardening is minor, and the other factors affecting strain-age hardening must be optimized simultaneously to show a coaxing effect. In addition, the degree of coaxing effect of smooth steel specimens was predominantly controlled by the intergranular fatigue crack initiation behavior. Consequently, a considerable amount of solute carbon and an alternate process for the stress amplitude increment and aging time are required for strain-age hardening that suppresses intergranular fatigue crack initiation.

UR - http://www.scopus.com/inward/record.url?scp=85032801990&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85032801990&partnerID=8YFLogxK

U2 - 10.2355/tetsutohagane.TETSU-2017-043

DO - 10.2355/tetsutohagane.TETSU-2017-043

M3 - Article

AN - SCOPUS:85032801990

VL - 103

SP - 660

EP - 666

JO - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

JF - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

SN - 0021-1575

IS - 11

ER -