Mechanism of alumina-enhanced sintering of fine zirconia powder: Influence of alumina concentration on the initial stage sintering

Koji Matsui, Takanori Yamakawa, Masato Uehara, Naoya Enomoto, Junichi Hojo

Research output: Contribution to journalArticle

27 Citations (Scopus)

Abstract

The isothermal shrinkage behavior of 2.9 mol% Y2O 3-doped ZrO2 powders with 0-1 mass% Al2O 3 was investigated to clarify the effect of Al2O 3 concentration on the initial sintering stage. The shrinkage of the powder compact was measured at constant temperatures in the range of 950°-1050°C. The Al2O3 addition increased the densification rate with increasing temperature. The values of apparent activation energy (nQ) and apparent frequency-factor term (β 0n), where n is the order depending on the diffusion mechanism, were estimated at the initial sintering stage by applying a sintering-rate equation to the isothermal shrinkage data. The diffusion mechanism changed from grain-boundary diffusion (GBD) to volume diffusion (VD) by Al2O3 addition and both nQ and β0 n increased with increasing Al2O3 concentration. The kinetic analysis of the sintering mechanism suggested that the increase of densification rate by Al2O3 addition largely depends on the increase of β0n, that is, the increases of n with GBD→VD change and β0 with an increase in Al2O3 content, although the nQ also increases with Al2O3 addition. This enhanced sintering mechanism is reasonably interpreted by the segregated dissolution of Al2O 3 at ZrO2 grain boundaries.

Original languageEnglish
Pages (from-to)1888-1897
Number of pages10
JournalJournal of the American Ceramic Society
Volume91
Issue number6
DOIs
Publication statusPublished - Jun 1 2008

Fingerprint

Aluminum Oxide
Zirconia
Powders
Alumina
Sintering
Densification
Grain boundaries
Dissolution
Activation energy
zirconium oxide
Temperature
Kinetics

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

Cite this

Mechanism of alumina-enhanced sintering of fine zirconia powder : Influence of alumina concentration on the initial stage sintering. / Matsui, Koji; Yamakawa, Takanori; Uehara, Masato; Enomoto, Naoya; Hojo, Junichi.

In: Journal of the American Ceramic Society, Vol. 91, No. 6, 01.06.2008, p. 1888-1897.

Research output: Contribution to journalArticle

Matsui, Koji ; Yamakawa, Takanori ; Uehara, Masato ; Enomoto, Naoya ; Hojo, Junichi. / Mechanism of alumina-enhanced sintering of fine zirconia powder : Influence of alumina concentration on the initial stage sintering. In: Journal of the American Ceramic Society. 2008 ; Vol. 91, No. 6. pp. 1888-1897.
@article{fd5f34c5f8b54556a26bf990eb8a69d2,
title = "Mechanism of alumina-enhanced sintering of fine zirconia powder: Influence of alumina concentration on the initial stage sintering",
abstract = "The isothermal shrinkage behavior of 2.9 mol{\%} Y2O 3-doped ZrO2 powders with 0-1 mass{\%} Al2O 3 was investigated to clarify the effect of Al2O 3 concentration on the initial sintering stage. The shrinkage of the powder compact was measured at constant temperatures in the range of 950°-1050°C. The Al2O3 addition increased the densification rate with increasing temperature. The values of apparent activation energy (nQ) and apparent frequency-factor term (β 0n), where n is the order depending on the diffusion mechanism, were estimated at the initial sintering stage by applying a sintering-rate equation to the isothermal shrinkage data. The diffusion mechanism changed from grain-boundary diffusion (GBD) to volume diffusion (VD) by Al2O3 addition and both nQ and β0 n increased with increasing Al2O3 concentration. The kinetic analysis of the sintering mechanism suggested that the increase of densification rate by Al2O3 addition largely depends on the increase of β0n, that is, the increases of n with GBD→VD change and β0 with an increase in Al2O3 content, although the nQ also increases with Al2O3 addition. This enhanced sintering mechanism is reasonably interpreted by the segregated dissolution of Al2O 3 at ZrO2 grain boundaries.",
author = "Koji Matsui and Takanori Yamakawa and Masato Uehara and Naoya Enomoto and Junichi Hojo",
year = "2008",
month = "6",
day = "1",
doi = "10.1111/j.1551-2916.2008.02350.x",
language = "English",
volume = "91",
pages = "1888--1897",
journal = "Journal of the American Ceramic Society",
issn = "0002-7820",
publisher = "Wiley-Blackwell",
number = "6",

}

TY - JOUR

T1 - Mechanism of alumina-enhanced sintering of fine zirconia powder

T2 - Influence of alumina concentration on the initial stage sintering

AU - Matsui, Koji

AU - Yamakawa, Takanori

AU - Uehara, Masato

AU - Enomoto, Naoya

AU - Hojo, Junichi

PY - 2008/6/1

Y1 - 2008/6/1

N2 - The isothermal shrinkage behavior of 2.9 mol% Y2O 3-doped ZrO2 powders with 0-1 mass% Al2O 3 was investigated to clarify the effect of Al2O 3 concentration on the initial sintering stage. The shrinkage of the powder compact was measured at constant temperatures in the range of 950°-1050°C. The Al2O3 addition increased the densification rate with increasing temperature. The values of apparent activation energy (nQ) and apparent frequency-factor term (β 0n), where n is the order depending on the diffusion mechanism, were estimated at the initial sintering stage by applying a sintering-rate equation to the isothermal shrinkage data. The diffusion mechanism changed from grain-boundary diffusion (GBD) to volume diffusion (VD) by Al2O3 addition and both nQ and β0 n increased with increasing Al2O3 concentration. The kinetic analysis of the sintering mechanism suggested that the increase of densification rate by Al2O3 addition largely depends on the increase of β0n, that is, the increases of n with GBD→VD change and β0 with an increase in Al2O3 content, although the nQ also increases with Al2O3 addition. This enhanced sintering mechanism is reasonably interpreted by the segregated dissolution of Al2O 3 at ZrO2 grain boundaries.

AB - The isothermal shrinkage behavior of 2.9 mol% Y2O 3-doped ZrO2 powders with 0-1 mass% Al2O 3 was investigated to clarify the effect of Al2O 3 concentration on the initial sintering stage. The shrinkage of the powder compact was measured at constant temperatures in the range of 950°-1050°C. The Al2O3 addition increased the densification rate with increasing temperature. The values of apparent activation energy (nQ) and apparent frequency-factor term (β 0n), where n is the order depending on the diffusion mechanism, were estimated at the initial sintering stage by applying a sintering-rate equation to the isothermal shrinkage data. The diffusion mechanism changed from grain-boundary diffusion (GBD) to volume diffusion (VD) by Al2O3 addition and both nQ and β0 n increased with increasing Al2O3 concentration. The kinetic analysis of the sintering mechanism suggested that the increase of densification rate by Al2O3 addition largely depends on the increase of β0n, that is, the increases of n with GBD→VD change and β0 with an increase in Al2O3 content, although the nQ also increases with Al2O3 addition. This enhanced sintering mechanism is reasonably interpreted by the segregated dissolution of Al2O 3 at ZrO2 grain boundaries.

UR - http://www.scopus.com/inward/record.url?scp=44649146396&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=44649146396&partnerID=8YFLogxK

U2 - 10.1111/j.1551-2916.2008.02350.x

DO - 10.1111/j.1551-2916.2008.02350.x

M3 - Article

AN - SCOPUS:44649146396

VL - 91

SP - 1888

EP - 1897

JO - Journal of the American Ceramic Society

JF - Journal of the American Ceramic Society

SN - 0002-7820

IS - 6

ER -