Mechanism of plastic deformation of Mn-added TiAl L10-type intermetallic compound

T. Hanamura, R. Uemori, M. Tanino

Research output: Contribution to journalArticle

93 Citations (Scopus)

Abstract

Titanium aluminum intermetallic compound is a possible candidate for a high-temperature structural material, except for a problem of lack of room-temperature ductility. Recently, this problem was found to be overcome possibly by the addition of Mn, but this mechanism has not been fully understood yet. In order to understand the fundamental mechanism of the ductility improvement by Mn addition, microanalyses have been carried out. The results are as follows. Twin structures in a TiAl intermetallic compound in the as-cast state can be eliminated by high-temperature annealing, while those in Mn-added TiAl are thermally more stable and exist even after annealing for 86.4 ks at 1273 K. The reason for this thermal stabilization of twin structures is considered to be due to the pinning effect of twin dislocations by Mn addition. The enhancement of twin deformation in TiAl by Mn addition is regarded to be caused by two factors. One is the stabilization of twin partial dislocations, becoming the nucleation sites for twin formation. The other is the decrease in stacking fault energy, which makes twin deformation energetically easier.

Original languageEnglish
Pages (from-to)656-664
Number of pages9
JournalJournal of Materials Research
Volume3
Issue number4
DOIs
Publication statusPublished - Sep 1988
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Mechanism of plastic deformation of Mn-added TiAl L1<sub>0</sub>-type intermetallic compound'. Together they form a unique fingerprint.

  • Cite this