Metalorganic chemical vapor deposition of epitaxial perovskite SrIrO 3 films on (100)SrTiO3 substrates

Yong Kwan Kim, Akihiro Sumi, Kenji Takahashi, Shintaro Yokoyama, Shinichi Ito, Takayuki Watanabe, Kensuke Akiyama, Satoru Kaneko, Keisuke Saito, Hiroshi Funakubo

Research output: Contribution to journalArticlepeer-review

29 Citations (Scopus)

Abstract

(001)c-oriented 60-70-nm-thick SrIO3films with a high-pressure-stable perovskite phase were epitaxially grown on (100)SrTiO 3 substrates by metalorganic chemical vapor deposition, and the crystal structure and the resistivity of the films were investigated. X-ray diffraction techniques including general θ-2θ scan, the rocking curve and high-resolution reciprocal space mapping, were used to determine crystal quality, lattice constant, and crystal structure of the SrIrO 3 films. It was demonstrated that the film crystal structure was tetragonal distorted by strong mechanical constraints due to the in-plane matching with the lattice parameters of SrTiO3 substrates, and maintained almost the same unit cell volume as the reported one for the perovskite cubic SrIrO3 phase. The resistivity of the film at room temperature was 740 μΩ cm, and it decreased with decreasing temperature down to 100 K. Finally, an atomically flat surface was obtained on atomically stepped (100)SrTiO3 substrates.

Original languageEnglish
Pages (from-to)L36-L38
JournalJapanese Journal of Applied Physics, Part 2: Letters
Volume45
Issue number1-3
DOIs
Publication statusPublished - Jan 31 2006
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Engineering(all)
  • Physics and Astronomy (miscellaneous)
  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Metalorganic chemical vapor deposition of epitaxial perovskite SrIrO <sub>3</sub> films on (100)SrTiO<sub>3</sub> substrates'. Together they form a unique fingerprint.

Cite this