Microscopic and macroscopic damage in metals exposed to LHD divertor plasmas

M. Tokitani, M. Miyamoto, D. Koga, K. Tokunaga, T. Fujiwara, N. Yoshida, S. Masuzaki, N. Ashikawa, T. Morisaki, M. Shoji, A. Komori

Research output: Contribution to journalArticle

20 Citations (Scopus)

Abstract

In order to study erosion/damage processes of the tungsten divertor target, material probe experiments were carried out by exposing tungsten specimens to short pulse helium or hydrogen divertor plasma in LHD (10-20 eV, about 1 × 1022 ions/m2 s). A narrow 'footprint', a trace of local-melting, of divertor plasma was formed on the material probe head along the divertor-leg for both hydrogen and helium discharges. In the specimens located rather far from the footprint, where less loading of particles is expected, remarkable blistering was confirmed for both helium and hydrogen irradiation cases. The erosion of the surface was estimated to be 6.3 nm/1 s (one discharge), and 4.1 nm/24 s (19 discharges) for helium and hydrogen, respectively. One should note that erosion due to blistering occurs even for the very low energy hydrogen plasma exposure. It is considered that the abrupt change of specimen temperature due to very high flux particle load may enhance the blistering.

Original languageEnglish
Pages (from-to)937-941
Number of pages5
JournalJournal of Nuclear Materials
Volume337-339
Issue number1-3 SPEC. ISS.
DOIs
Publication statusPublished - Mar 1 2005

All Science Journal Classification (ASJC) codes

  • Nuclear and High Energy Physics
  • Materials Science(all)
  • Nuclear Energy and Engineering

Fingerprint Dive into the research topics of 'Microscopic and macroscopic damage in metals exposed to LHD divertor plasmas'. Together they form a unique fingerprint.

  • Cite this

    Tokitani, M., Miyamoto, M., Koga, D., Tokunaga, K., Fujiwara, T., Yoshida, N., Masuzaki, S., Ashikawa, N., Morisaki, T., Shoji, M., & Komori, A. (2005). Microscopic and macroscopic damage in metals exposed to LHD divertor plasmas. Journal of Nuclear Materials, 337-339(1-3 SPEC. ISS.), 937-941. https://doi.org/10.1016/j.jnucmat.2004.07.054