Nanoindentation characterization of intermetallic compounds formed at Sn-Cu (-Ni) solder/Cu substrate interfaces

H. Tsukamoto, Z. Dong, H. Huang, T. Nishimura, K. Nogita

Research output: Contribution to journalConference article

Abstract

The formation of intermetallic compounds (IMCs) at solder/substrate interfaces is essential, which have a critical effect on the mechanical reliability of solder joints. In this study, nanoindentation was used to investigate elastic modulus, hardness and creep properties of the IMCs formed at the interface between Sn-Cu (-Ni) solder ball grid arrays (BGAs) and Cu substrates in multiple-reflowed samples. All the tests were conducted at room temperature. The elastic modulus and hardness of (Cu,Ni)6Sn 5 were higher than those of Cu6Sn5. The hardnesses of (Cu,Ni)6Sn5 were scattered, which may be attributed to the crystallographic characteristics such as a growth texture of the IMCs. The creep stress exponents of the IMCs were extremely high (9.5∼44), compared to pure tin and solder alloys.

Original languageEnglish
Pages (from-to)131-137
Number of pages7
JournalMaterials Forum
Volume34
Publication statusPublished - Dec 1 2008
Event2009 Materials and AustCeram Conference, MAC 2009 - Gold Coast, QLD, Australia
Duration: Jul 1 2009Jul 3 2009

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Nanoindentation characterization of intermetallic compounds formed at Sn-Cu (-Ni) solder/Cu substrate interfaces'. Together they form a unique fingerprint.

  • Cite this

    Tsukamoto, H., Dong, Z., Huang, H., Nishimura, T., & Nogita, K. (2008). Nanoindentation characterization of intermetallic compounds formed at Sn-Cu (-Ni) solder/Cu substrate interfaces. Materials Forum, 34, 131-137.