Nanostructural analyses of intra- and intergranular precipitates in high-temperature heat-treated nitrogen-added austenitic stainless steel

Minoru Ochi, Kousei Sato, Ryo Teranishi, Yukio Sato, Jun Ichi Hamada, Chikako Takushima, Toru Hara, Kenji Kaneko

    Research output: Contribution to journalArticlepeer-review

    1 Citation (Scopus)

    Abstract

    More than one thousand intragranular and intergranular precipitates of nitrogen-added austenitic stainless steel, SUSXM15J1, were characterized by FIB-SEM serial-sectioning tomography, by conventional transmission electron microscopy (TEM) and by scanning transmission electron microscopy (STEM). All of intragranular precipitates were found nitrided to form dichromium nitride, Cr2N, two types of intergranular precipitates were found Cr2N and Cr3Ni2Si(N), and some of them were grown and jointed due to the additional heat treatment during the tensile test at 1 173 K, which probably contributed to its high-temperature strength.

    Original languageEnglish
    Pages (from-to)1459-1466
    Number of pages8
    Journalisij international
    Volume58
    Issue number8
    DOIs
    Publication statusPublished - Aug 15 2018

    All Science Journal Classification (ASJC) codes

    • Mechanics of Materials
    • Mechanical Engineering
    • Metals and Alloys
    • Materials Chemistry

    Fingerprint

    Dive into the research topics of 'Nanostructural analyses of intra- and intergranular precipitates in high-temperature heat-treated nitrogen-added austenitic stainless steel'. Together they form a unique fingerprint.

    Cite this