NASICON devices attached with Li2CO3-BaCO3 auxiliary phase for CO2 sensing under ambient conditions

K. Obata, K. Shimanoe, N. Miura, N. Yamazoe

Research output: Contribution to journalArticle

8 Citations (Scopus)

Abstract

NASICON (Na3Zr2Si2PO12) - based electrochemical devices, constructed in a gas-separation type or planar type, were attached with a Li2CO3-BaCO3 (1:2 in molar ratio) auxiliary phase to investigate their CO2 sensing properties under ambient conditions. The devices were found to be far more resistant to the disturbance by a change in relative humidity (RH) than those using Na2CO3 or NaHCO3 auxiliary phase. The EMF was correlated linearly with the logarithm of CO2 concentration in the range of 0.03-50% CO2 at 30°C, and the linear correlation shifted up or down only slightly with a change in RH between 30 and 90%. For a change in operating temperature, the CO2 sensing capability was kept almost the same at 45°C, while it was deteriorated significantly at 60 and 75°C, especially in the lower RH range. Applicability of a cobalt oxide bronze (Na0.6CoO2) as a solid reference electrode for the planar type device was also investigated. The devices using the bronze reference electrode exhibited the CO2 sensing capability as good as those using the Au reference electrode did. In addition, the bronze electrode was found to much improve the reproducibility of the EMF to a fixed concentration of CO2 among devices.

Original languageEnglish
Pages (from-to)4283-4288
Number of pages6
JournalJournal of Materials Science
Volume38
Issue number21
DOIs
Publication statusPublished - Nov 1 2003

Fingerprint

Bronze
Atmospheric humidity
Electrodes
Electric potential
Cobalt
Gases
Oxides
Temperature

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

NASICON devices attached with Li2CO3-BaCO3 auxiliary phase for CO2 sensing under ambient conditions. / Obata, K.; Shimanoe, K.; Miura, N.; Yamazoe, N.

In: Journal of Materials Science, Vol. 38, No. 21, 01.11.2003, p. 4283-4288.

Research output: Contribution to journalArticle

@article{11de50c24b1a4b0ebec90f49c20b9c51,
title = "NASICON devices attached with Li2CO3-BaCO3 auxiliary phase for CO2 sensing under ambient conditions",
abstract = "NASICON (Na3Zr2Si2PO12) - based electrochemical devices, constructed in a gas-separation type or planar type, were attached with a Li2CO3-BaCO3 (1:2 in molar ratio) auxiliary phase to investigate their CO2 sensing properties under ambient conditions. The devices were found to be far more resistant to the disturbance by a change in relative humidity (RH) than those using Na2CO3 or NaHCO3 auxiliary phase. The EMF was correlated linearly with the logarithm of CO2 concentration in the range of 0.03-50{\%} CO2 at 30°C, and the linear correlation shifted up or down only slightly with a change in RH between 30 and 90{\%}. For a change in operating temperature, the CO2 sensing capability was kept almost the same at 45°C, while it was deteriorated significantly at 60 and 75°C, especially in the lower RH range. Applicability of a cobalt oxide bronze (Na0.6CoO2) as a solid reference electrode for the planar type device was also investigated. The devices using the bronze reference electrode exhibited the CO2 sensing capability as good as those using the Au reference electrode did. In addition, the bronze electrode was found to much improve the reproducibility of the EMF to a fixed concentration of CO2 among devices.",
author = "K. Obata and K. Shimanoe and N. Miura and N. Yamazoe",
year = "2003",
month = "11",
day = "1",
doi = "10.1023/A:1026322813276",
language = "English",
volume = "38",
pages = "4283--4288",
journal = "Journal of Materials Science",
issn = "0022-2461",
publisher = "Springer Netherlands",
number = "21",

}

TY - JOUR

T1 - NASICON devices attached with Li2CO3-BaCO3 auxiliary phase for CO2 sensing under ambient conditions

AU - Obata, K.

AU - Shimanoe, K.

AU - Miura, N.

AU - Yamazoe, N.

PY - 2003/11/1

Y1 - 2003/11/1

N2 - NASICON (Na3Zr2Si2PO12) - based electrochemical devices, constructed in a gas-separation type or planar type, were attached with a Li2CO3-BaCO3 (1:2 in molar ratio) auxiliary phase to investigate their CO2 sensing properties under ambient conditions. The devices were found to be far more resistant to the disturbance by a change in relative humidity (RH) than those using Na2CO3 or NaHCO3 auxiliary phase. The EMF was correlated linearly with the logarithm of CO2 concentration in the range of 0.03-50% CO2 at 30°C, and the linear correlation shifted up or down only slightly with a change in RH between 30 and 90%. For a change in operating temperature, the CO2 sensing capability was kept almost the same at 45°C, while it was deteriorated significantly at 60 and 75°C, especially in the lower RH range. Applicability of a cobalt oxide bronze (Na0.6CoO2) as a solid reference electrode for the planar type device was also investigated. The devices using the bronze reference electrode exhibited the CO2 sensing capability as good as those using the Au reference electrode did. In addition, the bronze electrode was found to much improve the reproducibility of the EMF to a fixed concentration of CO2 among devices.

AB - NASICON (Na3Zr2Si2PO12) - based electrochemical devices, constructed in a gas-separation type or planar type, were attached with a Li2CO3-BaCO3 (1:2 in molar ratio) auxiliary phase to investigate their CO2 sensing properties under ambient conditions. The devices were found to be far more resistant to the disturbance by a change in relative humidity (RH) than those using Na2CO3 or NaHCO3 auxiliary phase. The EMF was correlated linearly with the logarithm of CO2 concentration in the range of 0.03-50% CO2 at 30°C, and the linear correlation shifted up or down only slightly with a change in RH between 30 and 90%. For a change in operating temperature, the CO2 sensing capability was kept almost the same at 45°C, while it was deteriorated significantly at 60 and 75°C, especially in the lower RH range. Applicability of a cobalt oxide bronze (Na0.6CoO2) as a solid reference electrode for the planar type device was also investigated. The devices using the bronze reference electrode exhibited the CO2 sensing capability as good as those using the Au reference electrode did. In addition, the bronze electrode was found to much improve the reproducibility of the EMF to a fixed concentration of CO2 among devices.

UR - http://www.scopus.com/inward/record.url?scp=0344153287&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0344153287&partnerID=8YFLogxK

U2 - 10.1023/A:1026322813276

DO - 10.1023/A:1026322813276

M3 - Article

AN - SCOPUS:0344153287

VL - 38

SP - 4283

EP - 4288

JO - Journal of Materials Science

JF - Journal of Materials Science

SN - 0022-2461

IS - 21

ER -