Near-zero sintering shrinkage in pottery with wollastonite addition

Dong Hao, Takashi Akatsu, Nobuaki Kamochi, Miki Inada, Atsunori Shiraishi

Research output: Contribution to journalArticlepeer-review

Abstract

The precise control of the geometry of pottery is a challenge owing to the undesirable shrinkage and deformation observed after firing. In this study, near-zero sintering shrinkage pottery (NZS) with the sintering shrinkage (SS) of < 2.0% and pyroplastic deformation index (PI) of < 1.5 × 10−6 mm−1 was developed with varying amounts of added alumina and wollastonite. Wollastonite promotes anorthite crystallisation, thereby preventing sintering shrinkage at ∼1200 °C. The mechanism for the suppressed liquid-phase sintering of the pottery was also analysed. Moreover, NZS were obtained after firing at 1300 °C with a specific phase composition for suppressing the pyroplastic deformation. Thus, NZS was successfully prepared through liquid sintering from natural minerals. Therefore, this study provides a guide for the fabrication of earthenware, stoneware, unglazed porcelain and ceramic tiles with precise dimension and geometry. Additionally, it is also important for reducing the production loss in huge pottery and large-scale production by countering the sintering shrinkage.

Original languageEnglish
Pages (from-to)700-707
Number of pages8
JournalJournal of the European Ceramic Society
Volume43
Issue number2
DOIs
Publication statusPublished - Feb 2023

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

Fingerprint

Dive into the research topics of 'Near-zero sintering shrinkage in pottery with wollastonite addition'. Together they form a unique fingerprint.

Cite this