Ni-Fe alloy-supported intermediate temperature SOFCs using LaGaO3 electrolyte film for quick startup

Tatsumi Ishihara, Jingwang Yan, Makiko Enoki, Sachio Okada, Hiroshige Matsumoto

Research output: Contribution to journalArticle

8 Citations (Scopus)

Abstract

Intermediate temperature solid oxide fuel cells (SOFCs), which are highly tolerant against a thermal cycle, are studied by using the Ni-Fe porous alloy substrate prepared by an in situ reduction. It was found that Ni-Fe alloy exhibits high activity against anodic reaction and suitable compatibility with LaGaO3 electrolyte. The electrolyte film of La0.9Sr0.1Ga0.8Mg0.2O3 (LSGM) and Sm0.2Ce0.8O2 (SDC) bilayer with 5 μm thickness was successfully prepared on the dense NiO-Fe2O3 composite anode. After a in situ reduction, the dense plate of NiO-Fe2O3 was changed to the porous Ni-Fe alloy substrate; however, the LSGM film can keep the dense state. The prepared Ni-Fe alloy that supported LSGM cell demonstrated the maximum power densities of 0.9 W/cm2 and 0.4 W/cm2 at 873 K and 573 K. After heating up to 873 K within 540 s, there is no crack formed on the film and almost the theoretical open circuit voltage was exhibited. In addition, the maximum power density of 400 mW/cm2 was achieved at 773 K. After the thermal cycling, the decrease in the maximum power density was not large, and this suggests that the film is still gas tight and highly tolerant against the thermal cycle. Quick start characteristics of the metal support SOFC could expand the SOFC application to the electric source of a mobile-field-like automobile.

Original languageEnglish
Pages (from-to)312051-312053
Number of pages3
JournalJournal of Fuel Cell Science and Technology
Volume5
Issue number3
Publication statusPublished - Aug 1 2008

Fingerprint

Solid oxide fuel cells (SOFC)
Electrolytes
Temperature
Thermal cycling
Open circuit voltage
Substrates
Automobiles
Anodes
Gases
Metals
Cracks
Heating
Composite materials
Hot Temperature

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Renewable Energy, Sustainability and the Environment
  • Energy Engineering and Power Technology
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Ni-Fe alloy-supported intermediate temperature SOFCs using LaGaO3 electrolyte film for quick startup. / Ishihara, Tatsumi; Yan, Jingwang; Enoki, Makiko; Okada, Sachio; Matsumoto, Hiroshige.

In: Journal of Fuel Cell Science and Technology, Vol. 5, No. 3, 01.08.2008, p. 312051-312053.

Research output: Contribution to journalArticle

@article{d3ad3da50cc041d68efb790b06daaf84,
title = "Ni-Fe alloy-supported intermediate temperature SOFCs using LaGaO3 electrolyte film for quick startup",
abstract = "Intermediate temperature solid oxide fuel cells (SOFCs), which are highly tolerant against a thermal cycle, are studied by using the Ni-Fe porous alloy substrate prepared by an in situ reduction. It was found that Ni-Fe alloy exhibits high activity against anodic reaction and suitable compatibility with LaGaO3 electrolyte. The electrolyte film of La0.9Sr0.1Ga0.8Mg0.2O3 (LSGM) and Sm0.2Ce0.8O2 (SDC) bilayer with 5 μm thickness was successfully prepared on the dense NiO-Fe2O3 composite anode. After a in situ reduction, the dense plate of NiO-Fe2O3 was changed to the porous Ni-Fe alloy substrate; however, the LSGM film can keep the dense state. The prepared Ni-Fe alloy that supported LSGM cell demonstrated the maximum power densities of 0.9 W/cm2 and 0.4 W/cm2 at 873 K and 573 K. After heating up to 873 K within 540 s, there is no crack formed on the film and almost the theoretical open circuit voltage was exhibited. In addition, the maximum power density of 400 mW/cm2 was achieved at 773 K. After the thermal cycling, the decrease in the maximum power density was not large, and this suggests that the film is still gas tight and highly tolerant against the thermal cycle. Quick start characteristics of the metal support SOFC could expand the SOFC application to the electric source of a mobile-field-like automobile.",
author = "Tatsumi Ishihara and Jingwang Yan and Makiko Enoki and Sachio Okada and Hiroshige Matsumoto",
year = "2008",
month = "8",
day = "1",
language = "English",
volume = "5",
pages = "312051--312053",
journal = "Journal of Fuel Cell Science and Technology",
issn = "1550-624X",
publisher = "American Society of Mechanical Engineers(ASME)",
number = "3",

}

TY - JOUR

T1 - Ni-Fe alloy-supported intermediate temperature SOFCs using LaGaO3 electrolyte film for quick startup

AU - Ishihara, Tatsumi

AU - Yan, Jingwang

AU - Enoki, Makiko

AU - Okada, Sachio

AU - Matsumoto, Hiroshige

PY - 2008/8/1

Y1 - 2008/8/1

N2 - Intermediate temperature solid oxide fuel cells (SOFCs), which are highly tolerant against a thermal cycle, are studied by using the Ni-Fe porous alloy substrate prepared by an in situ reduction. It was found that Ni-Fe alloy exhibits high activity against anodic reaction and suitable compatibility with LaGaO3 electrolyte. The electrolyte film of La0.9Sr0.1Ga0.8Mg0.2O3 (LSGM) and Sm0.2Ce0.8O2 (SDC) bilayer with 5 μm thickness was successfully prepared on the dense NiO-Fe2O3 composite anode. After a in situ reduction, the dense plate of NiO-Fe2O3 was changed to the porous Ni-Fe alloy substrate; however, the LSGM film can keep the dense state. The prepared Ni-Fe alloy that supported LSGM cell demonstrated the maximum power densities of 0.9 W/cm2 and 0.4 W/cm2 at 873 K and 573 K. After heating up to 873 K within 540 s, there is no crack formed on the film and almost the theoretical open circuit voltage was exhibited. In addition, the maximum power density of 400 mW/cm2 was achieved at 773 K. After the thermal cycling, the decrease in the maximum power density was not large, and this suggests that the film is still gas tight and highly tolerant against the thermal cycle. Quick start characteristics of the metal support SOFC could expand the SOFC application to the electric source of a mobile-field-like automobile.

AB - Intermediate temperature solid oxide fuel cells (SOFCs), which are highly tolerant against a thermal cycle, are studied by using the Ni-Fe porous alloy substrate prepared by an in situ reduction. It was found that Ni-Fe alloy exhibits high activity against anodic reaction and suitable compatibility with LaGaO3 electrolyte. The electrolyte film of La0.9Sr0.1Ga0.8Mg0.2O3 (LSGM) and Sm0.2Ce0.8O2 (SDC) bilayer with 5 μm thickness was successfully prepared on the dense NiO-Fe2O3 composite anode. After a in situ reduction, the dense plate of NiO-Fe2O3 was changed to the porous Ni-Fe alloy substrate; however, the LSGM film can keep the dense state. The prepared Ni-Fe alloy that supported LSGM cell demonstrated the maximum power densities of 0.9 W/cm2 and 0.4 W/cm2 at 873 K and 573 K. After heating up to 873 K within 540 s, there is no crack formed on the film and almost the theoretical open circuit voltage was exhibited. In addition, the maximum power density of 400 mW/cm2 was achieved at 773 K. After the thermal cycling, the decrease in the maximum power density was not large, and this suggests that the film is still gas tight and highly tolerant against the thermal cycle. Quick start characteristics of the metal support SOFC could expand the SOFC application to the electric source of a mobile-field-like automobile.

UR - http://www.scopus.com/inward/record.url?scp=48249141107&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=48249141107&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:48249141107

VL - 5

SP - 312051

EP - 312053

JO - Journal of Fuel Cell Science and Technology

JF - Journal of Fuel Cell Science and Technology

SN - 1550-624X

IS - 3

ER -