Numerical analysis of silica coating effect on Pt cathode catalyst in polymer electrolyte fuel cells

Kayoung Park, Magnus So, Masaki Goto, Sakae Takenaka, Yoshifumi Tsuge, Gen Inoue

Research output: Contribution to journalArticlepeer-review

Abstract

The effects of silica-coated Pt catalysts (SiO2/Pt/C) were investigated by experimental measurements and numerical analysis in order to obtain manufacturing guidelines by designing optimized catalyst layers (CL) for polymer electrolyte fuel cells. The silica-coated Pt catalysts with hydrophilic silica layers were experimentally prepared and measured by a single cell. Experimental results showed lower performance of SiO2/Pt/C than non-coated Pt catalysts (Pt/C) under relative humidity (RH) of 80% at 80°C. In the simulation of the SiO2/Pt/C, two parameters including the enhancement of proton conductivity and an increase in the oxygen diffusion resistance in the CL, attributed to silica layers, were added. The distribution of current density at 0.8 A/sq cm of the SiO2/Pt/C at each humidity condition (100%RH, 80%RH, 60%RH, 40%RH) was more homogeneous and reached closer to the gas diffusion layer compared to those of the Pt/C. The result indicates that it is possible to improve durability by increasing the reaction located near the polymer electrolyte membrane. For both catalysts, the overvoltages at 0.8 A/sq cm were similar to each other, except for that of proton resistance in ionomer and oxygen diffusion in the ionomer.

Original languageEnglish
Pages (from-to)226-231
Number of pages6
JournalJOURNAL OF CHEMICAL ENGINEERING OF JAPAN
Volume54
Issue number5
DOIs
Publication statusPublished - May 20 2021

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Chemical Engineering(all)

Fingerprint

Dive into the research topics of 'Numerical analysis of silica coating effect on Pt cathode catalyst in polymer electrolyte fuel cells'. Together they form a unique fingerprint.

Cite this