OS0527 パーライト鋼平滑材における疲労き裂発生起点解析方法の体系化(OS5-6 応力集中・き裂発生,OS-5 材料の疲労挙動と損傷評価2)

Translated title of the contribution: OS0527 Systematization of Analysis Method of Fatigue Crack Initiation Site in Pearlitic Steel Smooth Specimen

濱田 繁, 佐々木 大輔, 中田 伸生, 土山 聡宏, 上田 正治, 高島 和希, 野口 博司

Research output: Contribution to journalArticle

Abstract

In order to systemize the analysis method of fatigue crack initiation origin (fatigue failure maximum weak part), fatigue failure maximum weak part and the relationship to material texture were analyzed. Pearlitic steel smooth material was used for the material made into the example. First, a mechanical engineer's focus and technology were used, specification of a fatigue failure maximum weak part in pearlitic steel smooth material was performed, and relation between material texture and a fatigue failure maximum weak part was clarified. Then, analysis to material texture was carried out using the knowledge and analysis technology of crystallography of a metallurgist. A fatigue test and analysis showed that a flat face existed at the fatigue crack initiation origin of pearlitic steel smooth material. In addition, as a result of the analysis of a flat face, the formation mechanism of fatigue crack initiation origin (flat face) was able to be clarified, and systematization of analysis was able to be attained.
Translated title of the contributionOS0527 Systematization of Analysis Method of Fatigue Crack Initiation Site in Pearlitic Steel Smooth Specimen
Original languageJapanese
Pages (from-to)_OS0527-1_-_OS0527-3_
JournalM&M材料力学カンファレンス
Volume2011
Issue number0
DOIs
Publication statusPublished - 2011