Oxidation behavior of cyclohexane on alumina-supported manganese oxides with ozone

Hisahiro Einaga, Shigeru Futamura

Research output: Contribution to journalArticle

98 Citations (Scopus)

Abstract

Catalytic oxidation of cyclohexane with ozone was carried out over alumina-supported manganese oxides at 295 K. The catalytic activities decreased steeply with time on stream, and then reached a steady state. At the steady state, the mole fractions of CO2 and CO were 90 and 10%, respectively, with the carbon balance of around 50%. The decomposition ratio was estimated to be 8-10, independent of Mn loadings and support materials. Partially oxidized compounds including alcohols, ketones, acid anhydrides and carboxylic acids were formed on the catalyst surface. These compounds were decomposed by ozone feed. On the other hand, highly resistant species containing C=O, COO- and CH groups remained on the catalyst surface, which caused the gradual deactivation of the catalyst. The C=O groups were decomposed at relatively lower temperatures (<473 K), while higher temperature (>473 K) was necessary to decompose the COO- and CH groups.

Original languageEnglish
Pages (from-to)49-55
Number of pages7
JournalApplied Catalysis B: Environmental
Volume60
Issue number1-2
DOIs
Publication statusPublished - Sep 1 2005
Externally publishedYes

    Fingerprint

All Science Journal Classification (ASJC) codes

  • Catalysis
  • Environmental Science(all)
  • Process Chemistry and Technology

Cite this