Parameters for the evaluation of hydrogen embrittlement of high strength steel

Shusaku Takagi, Tadanobu Inoue, Toru Hara, Masao Hayakawa, Kaneaki Tsuzaki, Toshihiko Takahashi

Research output: Contribution to journalArticle

37 Citations (Scopus)

Abstract

The influences of the applied stress and the stress concentration factor (Kt) on hydrogen embrittlement were investigated in the commercial JIS SCM440 steel with the tensile strength of 1403 MPa. The applied stress was changed from 0.33 times to 0.72 times the tensile strength of the notched specimen, while the Kt was altered from 2.1 to 6.9. The hydrogen embrittlement property was evaluated with the resistance to the diffusible hydrogen in the steel. The diffusible hydrogen concentrations were analyzed by thermal desorption analysis. The results are as follows. (1) The hydrogen embrittlement occurs under the lower diffusible hydrogen concentrations with increasing Kt. However, the HD-t (diffusible hydrogen concentration-time to failure) curves become almost the same when the Kt and the applied stress are high. (2) The criterion of the hydrogen embrittlement cannot be determined by the combination of the maximum local axial stress in the specimen and the maximum diffusible hydrogen concentration locally accumulated in the specimen. In the discussion part, it was proposed that it is very important to consider the stress distribution in the specimen for the evaluation of hydrogen embrittlement.

Original languageEnglish
Pages (from-to)689-695
Number of pages7
JournalTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
Volume86
Issue number10
DOIs
Publication statusPublished - Jan 1 2000

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Parameters for the evaluation of hydrogen embrittlement of high strength steel'. Together they form a unique fingerprint.

  • Cite this